Abstract:Abstract Porous three-dimensional SiC/melamine-derived carbon foam (3D-SiC/MDCF) composite with an original open pore structure was fabricated by the heat treatment of the commercial melamine foam (MF), carbonization of the stable MF, and chemical vapor deposition of the ultra-thin SiC coating. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) were employed to detect the microstructure and morphology of the as-prepared composites. The results indicated that the 3D-SiC/MDCF composites with the coating structure were prepared successfully. The obtained minimum reflection loss was -29.50 dB when the frequency and absorption thickness were 11.36 GHz and 1.75 mm, respectively. Further, a novel strategy was put forward to state that the best microwave absorption property with a thin thickness of 1.65 mm was gained, where the minimum reflection loss was -24.51 dB and the frequency bandwidth was 3.08 GHz. The excellent electromagnetic wave absorption ability resulted from the specific cladding structure, which could change the raw dielectric property to acquire excellent impedance matching. This present work had a certain extend reference meaning for the potential applications of the lightweight wave absorption materials with target functionalities.

What problem does this paper attempt to address?

The paper attempts to address the problem of developing a lightweight material with excellent electromagnetic wave absorption capabilities. Specifically, the authors prepared three-dimensional porous SiC/melamine-derived carbon foam (3D-SiC/MDCF) composites through heat treatment, carbonization, and chemical vapor deposition (CVD) techniques, and studied their microstructure and electromagnetic wave absorption properties. ### Main Issues: 1. **Development of high-performance electromagnetic wave absorbing materials**: With the rapid development of electromagnetic wave technology, various electromagnetic interferences pose a threat to the normal operation of electronic devices. Therefore, it is particularly important to develop effective microwave absorbing materials. 2. **Improving the lightweight and absorption performance of materials**: Existing microwave absorbing materials have deficiencies in terms of lightweight and absorption performance, necessitating the development of new materials and preparation methods to meet practical application needs. 3. **Optimizing the microstructure of materials**: The microstructure of materials has a significant impact on their electromagnetic wave absorption performance, so it is necessary to improve the electromagnetic wave absorption capability of materials through reasonable microstructure adjustments. ### Solutions: - **Material selection and preparation**: Commercial melamine foam (MF) was selected as the precursor, and 3D-SiC/MDCF composites were prepared through heat treatment, carbonization, and CVD techniques. - **Microstructure analysis**: The microstructure and morphology of the materials were detected using scanning electron microscopy (SEM) and X-ray diffraction (XRD). - **Electromagnetic wave absorption performance testing**: The dielectric constant and reflection loss of the materials were tested using a vector network analyzer (VNA) to evaluate their electromagnetic wave absorption performance. ### Main Achievements: - Successfully prepared 3D-SiC/MDCF composites, with a minimum reflection loss of -29.50 dB, an absorption thickness of 1.75 mm, and an effective bandwidth of 2.64 GHz. - Proposed a novel strategy to determine the optimal absorption thickness by calculating the electromagnetic wave absorption efficiency (RE), showing that a sample with a thickness of 1.65 mm has the best electromagnetic wave absorption performance. ### Application Prospects: - The material features lightweight, high absorption performance, and wide bandwidth, and is expected to be widely used in aerospace, military, and civilian electronics fields.

Porous SiC/melamine-derived carbon foam frameworks with excellent electromagnetic wave absorbing capacity

Synthesis and microwave absorption properties of novel reticulation SiC/Porous melamine-derived carbon foam

Reticulated SiC Coating Reinforced Carbon Foam with Tunable Electromagnetic Microwave Absorption Performance

Novel Three-Dimensional SiC/Melamine-Derived Carbon Foam-Reinforced SiO2 Aerogel Composite with Low Dielectric Loss and High Impedance Matching Ratio

Enhanced Electromagnetic Absorption Properties of Novel 3D-CF/PyC Modified by Reticulated SiC Coating

High-efficiency and Wide-Bandwidth Microwave Absorbers Based on MoS2-coated Carbon Fiber

Effects of SiC coating on microwave absorption of novel three-dimensional reticulated SiC/porous carbon foam

Hollow SiC foam with a double interconnected network for superior microwave absorption ability

Carbon Foams Modified with In-Situ Formation of Si3N4 and SiC for Enhanced Electromagnetic Microwave Absorption Property and Thermostability

Microstructure and Microwave Absorption Performance Variation of SiC/C Foam at Different Elevated-Temperature Heat Treatment

Construction of SiCnws/carbon Foam Composites with Multiple Loss Mechanisms for Excellent Electromagnetic Wave Absorption

Environmentally Friendly a Multifunctional Cellulose-Based Carbon Foam for Superior Electromagnetic Wave Absorption Performance

Lightweight and salt spray corrosion resistant porous SiC/FeSiCr hybrids for enhanced microwave absorption in the C-band

The 3D CoNi alloy particles embedded in N-doped porous carbon foams for high-performance microwave absorbers

Constructing 3D Tent-Like frameworks in melamine hybrid foam for superior microwave absorption and thermal insulation

Enhanced microwave absorption performance originated from interface and unrivaled impedance matching of SiO 2 /carbon fiber

Double Network Nested Foam Composites With Tunable Electromagnetic Wave Absorption Performances

High-performance microwave absorption of MOF‐derived Co3O4@N-doped carbon anchored on carbon foam

Ultralight α–Si 3 N 4 w/SiC foam ceramics with superior microwave absorption performance in X- and Ku-bands

Ultralight Α–Si3n4w/Sic Foam Ceramics with Superior Microwave Absorption Performance in X- and Ku-Bands

Ultralight And High-Strength Sicnw@Sic Foam With Highly Efficient Microwave Absorption And Heat Insulation Properties