Preparation and investigation of mechanical and electromagnetic wave absorption properties of TiC–TiB2/Si3N4 composites
Shaoyin Wang,Jianqiang Bi,Guandong Liang,Linjing Qiao,Yao Yang,Hongyi Wang,Shuyong Liang,Jiacheng Rong,Chengjiao Che,Jilie Yuan,Yueguang Chen
DOI: https://doi.org/10.1111/jace.19925
IF: 4.186
2024-05-31
Journal of the American Ceramic Society
Abstract:(1) The preparation of TiC–TiB2/Si3N4 composites was achieved via pressureless sintering at a temperature of 1650°C for 2 h. (2) The 30 wt% TiC–TiB2/ Si3N4 composite exhibited notable characteristics with the bending strength of 93.11 ± 3.91 MPa, minimum reflection loss of −38.87 dB, and effective absorption bandwidth of 1.43 GHz in the Ku‐band. (3) This work paves the way for the preparation of composites with both satisfactory mechanical properties and electromagnetic wave absorption properties. The aim of achieving integration of lightweight, high strength, high‐temperature resistant, and satisfactory electromagnetic (EM) wave absorption was successfully accomplished in the present study by synthesizing TiC–TiB2 fibers reinforced Si3N4 composites, which were pressureless sintered at 1650°C for 2 h. The preparation of TiC–TiB2 fibers was conducted through a chloride‐assisted carbothermic method. This work focused on investigating the effects of incorporating TiC–TiB2 fibers on the mechanical properties and EM wave absorption characteristics of the composites. The 30 wt% TiC–TiB2/Si3N4 composite displayed the bulk density of 1.89 g/cm3, bending strength of 93.11 ± 3.91 MPa, fracture toughness of 1.81 ± 0.10 MPa m1/2, minimum reflection loss of −38.87 dB, and effective absorption bandwidth of 1.43 GHz in the Ku‐band, respectively. The as‐synthesized TiC–TiB2/Si3N4 composites are promising candidates for EM wave absorbing load‐bearing materials due to their outstanding mechanical properties and microwave absorption properties.
materials science, ceramics