Abstract:Synthetic tetrahedrite (Cu12Sb4S13) is considered a promising p-type thermoelectric material owing to its intrinsically low thermal conductivity, relative nontoxicity, and presence of light elements Cu and S. Since Cu12Sb4S13 has a high carrier (hole) concentration, its power factor can be optimized by decreasing the carrier concentration via doping. In this study, Zn doping is performed to optimize the power factor by reducing the carrier concentration, and Bi doping is performed to reduce the lattice thermal conductivity through additional phonon scattering by atomic mass fluctuation and lattice distortion. Cu12−xZnxSb4−ySbyS13 tetrahedrites (0.1 ≤ x ≤ 0.4 and 0.1 ≤ y ≤ 0.4) were prepared using mechanical alloying and hot pressing, and the effects of double doping of Zn and Bi on the charge transport and thermoelectric properties were examined. X-ray diffraction analysis revealed the successful formation of the tetrahedrite phase, but a small amount of skinnerite phase (Cu3SbS3) was produced with an increase in the Bi content. The lattice constant increased with an increase in Zn and Bi doping contents, as the ionic radii of Zn and Bi were larger than those of Cu and Sb, respectively. With an increase in the Zn content and a decrease in the Bi content, the carrier concentration decreased. Consequently, the electrical conductivity decreased, whereas the Seebeck coefficient increased. The decline in the electrical conductivity with Zn doping dominated the increase in the Seebeck coefficient, which in turn reduced the power factor. However, the power factor did not change significantly with a change in the Bi content. The lattice thermal conductivity was close to the theoretical minimum value in tetrahedrite upon substituting with Zn and Bi, and thus, the thermal conductivities of all the specimens were less than 0.94 Wm−1 K−1 at temperatures ranging from 323 to 723 K. Consequently, the dimensionless figure of merit, ZT = 0.77, was obtained for Cu11.9Zn0.1Sb3.9Bi0.1S13 at 723 K, which was attributed to a relatively high power factor (0.83 mWm−1 K−2) and low thermal conductivity (0.76 Wm−1 K−1).

Modification of tetrahedrite Cu12Sb4S13 thermoelectric performance via the combined treatment of mechanochemistry and composite formation

Electronic Transport and Thermoelectric Properties of Cu12-xZnxSb4S13 Tetrahedrites Prepared by Mechanical Alloying and Hot Pressing

Augmentation in the thermoelectric performance by integrating the natural minerals with synthetic tetrahedrite compounds

Achieving high power factor and thermoelectric performance through dual substitution of Zn and Se in tetrahedrites Cu<sub>12</sub>Sb<sub>4</sub>S<sub>13</sub>

Achieving a High Thermoelectric Performance of Tetrahedrites by Adjusting the Electronic Density of States and Enhancing Phonon Scattering

Achieving High Power Factor And Thermoelectric Performance Through Dual Substitution Of Zn And Se In Tetrahedrites Cu12sb4s13

ZnO-Nanoparticle-Dispersed Cu11.5Ni0.5Sb4S13−δ Tetrahedrite Composites with Enhanced Thermoelectric Performance

Evaluation of Processing Parameters in the Solvothermal Synthesis of Cu-Rich Tetrahedrites for Potential Application as Thermoelectric Materials

Mechanosynthesis and Thermoelectric Properties of Fe, Zn, and Cd-Doped P-Type Tetrahedrite: Cu12-xMxSb4S13

Enhanced performance of thermoelectric nanocomposites based on Cu12Sb4S13 tetrahedrite

Realizing the Ultralow Lattice Thermal Conductivity of Cu3SbSe4 Compound via Sulfur Alloying Effect

Enhanced thermoelectric performance of chalcopyrite nanocomposite via co-milling of synthetic and natural minerals

Synthesis of Fe-Doped Tetrahedrites Cu<sub>12-x</sub>Fe<sub>x</sub>Sb<sub>4</sub>S<sub>13</sub> and Characterization of Their Thermoelectric Properties

Thermoelectric Cu 12 Sb 4 S 13 ‐Based Synthetic Minerals with a Sublimation‐Derived Porous Network

Phase Tuning for Enhancing the Thermoelectric Performance of Solution-Synthesized Cu 2– x S

High thermoelectric performance realized in porous Cu1.8S based composites by Na2S addition

Enhancing thermoelectric and mechanical properties of p-type Cu3SbSe4-based materials via embedding nanoscale Sb2Se3

Thermoelectric Cu12 Sb4 S13 -Based Synthetic Minerals with a Sublimation-Derived Porous Network.

Enhanced figure of merit for famatinite Cu3SbSe4 via band structure tuning and hierarchical architecture

Effects of Zn/Bi Double Doping on the Charge Transport and Thermoelectric Properties of Tetrahedrites Cu 12− X Zn X Sb 4− Y Bi Y S 13

Enhanced Thermoelectric and Mechanical Performances in Sintered Bi0.48Sb1.52Te3-AgSbSe2 Composite.