Abstract:By employing a pulsed laser, laser cladding was performed on IN718 alloy pre-coated with CrCoNi-TiC/SiC powders and three defect-free coatings were prepared successfully. Microstructures of these coatings were subjected to dedicated characterization and well correlated with their surface performances (hardness/wear resistance). The CrCoNi coating was found to be predominantly composed of coarse grains. The addition of TiC and SiC powders will not only generate fine carbides dispersed in the coatings but also lead to the changes of grain and substructure morphologies through modifying the solidification thermodynamics in the cladding zone. The CrCoNi-TiC and the CrCoNi-SiC coatings have average grain sizes of 8.1 ± 7.9 μm and 6.6 ± 5.6 μm, respectively, much smaller than that of the CrCoNi coating (19.3 ± 19.2 μm), indicating effective grain refinement after incorporating such carbides. The average hardness values of CrCoNi-TiC and the CrCoNi-SiC coatings are measured as 315.9 ± 5.3 HV and 321.8 ± 8.6 HV, respectively, considerably higher than those of the CrCoNi coating (265.3 ± 6.9 HV) and the substrate (255.3 ± 4.5 HV). Both the composite coatings also have lower wear rates (6.6 × 10 −4 mm 3 ·N −1 ·m −1 for the CrCoNi-TiC coating and 2.9 × 10 −4 mm 3 ·N −1 ·m −1 for the CrCoNi-SiC coating) than the CrCoNi coating (9.3 × 10 −4 mm 3 ·N −1 ·m −1 ) and the IN718 substrate (11.1 × 10 −4 mm 3 ·N −1 ·m −1 ). Based on dedicated microstructural analyses, the synergistic strengthening effects due to grain refinement, second phase particles, and solid solution of alloying elements are found to have contributed to the superior surface performances of both the composite coatings, with the SiC demonstrated to be a more effective additive.

Repair of SiC coating on carbon/carbon composites by laser cladding technique

Laser ablation behavior of SiO2-Nd2O3/Si-SiC-MoSi2 coated C/C composites repaired by laser cladding

Effects of reflectivity on laser-ablation resistance of the laser-cladding repaired Nd2O3 modified SiO2 coatings on C/C composites

Convenient Reparation of SiC-Coated C/C Composites by the Slurry Painting Method

Enhanced oxidation resistance of Mo-modified Si-SiC coating on C/C composites by laser-inducing

Additively-manufactured multiphase coatings with laser protection ability for the repairing of MoSi2-SiC/SiC coated C/C composites

Fabrication of SiC particulates reinforced MoSi2 composite coating by laser cladding

Microstructure and corrosion-wear behaviors for laser cladding repaired martensitic stainless steels using Co-based and Ni-based powders

Analysis of oxidation behavior of laser cladding SiC-Ti based composite strengthening coating

Repair feasibility and performance enhancement analysis of Fe-based alloy coating on ductile iron surface by high-speed laser cladding

Fabrication of porous SiC nanostructured coatings on C/C composite by laser chemical vapor deposition for improving the thermal shock resistance

Microstructure and wear properties of TiC/FeCrBSi surface composite coating prepared by laser cladding

Microstructures and Properties of Laser Cladding Al-TiC-CeO₂ Composite Coatings

Effect of SiC and TiC content on microstructure and wear behavior of Ni-based composite coating manufactured by laser cladding on Ti-6Al-4V

In-Situ Synthesis of Mosi2/Sic Composite Coating by Laser Cladding

Subsurface damage inhibiting and synchronous removal behavior of C f /SiC composites with laser-induced controllable ablation during abrasive belt grinding

Microstructure and properties of Al–70Si alloy prepared by laser cladding

Improved antioxidative and mechanical properties of SiC coated C/C composites via a SiO2-SiC reticulated layer

Ablated surface morphology evolution of SiCp/Al composites irradiated by a nanosecond laser

Pulsed laser cladding on IN718 alloy using pre-coated CrCoNi-TiC/SiC powders for enhancing wear resistance

Research on Microstructure Properties of the TiC/Ni-Fe-Al Coating Prepared by Laser Cladding Technology