Abstract:In this work, a ∼220 μm-thick heterogeneous remelted layer is achieved in the coarse-grained AZ41 Mg alloy by the laser surface remelting treatment. Microstructural evolution observations reveal that the remelted heterogeneous layer consists of gradient refined equiaxed α-Mg grains (average grain size from ∼4.6 μm in the bottom to ∼ 60 nm at the surface) and dispersed block-shaped nanoscaled β-Mg17Al12 precipitations (∼22.8 nm), which is obviously different from the favored coarse dendritic or cellular α-Mg grains and lamellar β precipitations during conventional laser processing. The formation of this remelted layer is attributed to constitutional supercooling caused by solute elements and the thermal undercooling generated by the high cooling rates based on optimized processing parameters and liquid nitrogen cooling. The heterogeneous nanostructured remelted layer makes the laser-treated sample has a high hardness of 1.51 GPa, a yield strength of 230.4 MPa and an ultimate tensile strength of 313.7 MPa with a good ductility (12.5%). The laser-treated samples also show the higher fatigue lifetimes in low-cycle as well as high-cycle fatigue tests, which are respectively 2.3 and 18.6 times higher than the original samples. In addition, the laser-treated specimen exhibits a 25% higher fatigue limit compared with the original sample. The synergistic strengthening mechanism including gradient grain refinement and dispersed nanoscaled precipitations are quantitatively discussed to improve strength-ductility synergy and strain hardening capacity in the laser-treated samples. This mechanism could effectively facilitate resisting the initiation and propagation of the fatigue microcracks, which was further validated by the in-situ transmission electron microscope observations. Our results in this study could be further applied for the modification of grain morphology and precipitation distribution for additive manufacturing applications, critical to the development of advanced structural Mg alloys with high service performance in practical engineering environments.

Study on Porous Mg-Zn-Zr ZK61 Alloys Produced by Laser Additive Manufacturing

Formability, Microstructure, and Thermal Crack Characteristics of Selective Laser Melting of ZK60 Magnesium Alloy

Effect of 0.5 wt% Zr on defects, microstructure and mechanical properties of Al-3.6Zn-0.6Mg alloy fabricated by laser powder bed fusion

Effect of Aluminium Content and Processing Parameters on the Microstructure and Mechanical Properties of Laser Powder-Bed Fused Magnesium-Aluminium (0, 3, 6, 9wt%) Powder Mixture

Mechanical Properties of Selective Laser Melted ZK60 Alloy Enhanced by Nanoscale Precipitates with Core-Shell Structure

Selective Laser Melting of Mg-Zn Binary Alloys: Effects of Zn Content on Densification Behavior, Microstructure, and Mechanical Property

Additive manufacturing of ZK60 magnesium alloy by selective laser melting: Parameter optimization, microstructure and biodegradability

Laser Additive Manufacturing of Zn Porous Scaffolds: Shielding Gas Flow, Surface Quality and Densification

Effect of Zinc Content on Powder Characteristics, Porosity, Microstructure, and Corrosion Behavior of SLM-Printed Mg-xZn-0.2Mn Alloys for Biomedical Applications

Microstructure, Mechanical Properties and Multiphase Synergistic Strengthening Mechanisms of LPBF Fabricated AlZnMgZr Alloy with High Zn Content

Microstructural Evaluation and Tensile Properties of Al-Mg-Sc-Zr Alloys Prepared by LPBF

Microstructure evolution of laser powder bed fusion ZK60 Mg alloy after different heat treatment

Superior strength-ductility synergy and fatigue resistance of heterogeneous structured AZ41 Mg alloy by laser surface processing

Effects of magnesium on microstructure, properties and degradation behaviors of zinc-based alloys prepared by selective laser melting

Microstructure and mechanical properties of Al-Mg-Mn-Er-Zr alloys fabricated by laser powder bed fusion

Microstructure and Properties of a Nano-Zro2-reinforced AlSi10Mg Matrix Composite Prepared by Selective Laser Melting

Study on Corrosion Characteristics and Mechanism of Laser Powder Bed Fusion of Mg-Zn-Zr Alloy

Additive manufacturing of biodegradable Zn-xMg alloys: Effect of Mg content on manufacturability, microstructure and mechanical properties

Mechanical Properties of High Mg-Content Al-Mg-Sc-Zr Alloy Fabricated by Selective Laser Melting

Effects of processing parameters on fabrication defects, microstructure and mechanical properties of additive manufactured Mg–Nd–Zn–Zr alloy by selective laser melting process

A Study on Sc- and Zr-modified Al–Mg Alloys Processed by Selective Laser Melting