Abstract:In this work, a ∼220 μm-thick heterogeneous remelted layer is achieved in the coarse-grained AZ41 Mg alloy by the laser surface remelting treatment. Microstructural evolution observations reveal that the remelted heterogeneous layer consists of gradient refined equiaxed α-Mg grains (average grain size from ∼4.6 μm in the bottom to ∼ 60 nm at the surface) and dispersed block-shaped nanoscaled β-Mg17Al12 precipitations (∼22.8 nm), which is obviously different from the favored coarse dendritic or cellular α-Mg grains and lamellar β precipitations during conventional laser processing. The formation of this remelted layer is attributed to constitutional supercooling caused by solute elements and the thermal undercooling generated by the high cooling rates based on optimized processing parameters and liquid nitrogen cooling. The heterogeneous nanostructured remelted layer makes the laser-treated sample has a high hardness of 1.51 GPa, a yield strength of 230.4 MPa and an ultimate tensile strength of 313.7 MPa with a good ductility (12.5%). The laser-treated samples also show the higher fatigue lifetimes in low-cycle as well as high-cycle fatigue tests, which are respectively 2.3 and 18.6 times higher than the original samples. In addition, the laser-treated specimen exhibits a 25% higher fatigue limit compared with the original sample. The synergistic strengthening mechanism including gradient grain refinement and dispersed nanoscaled precipitations are quantitatively discussed to improve strength-ductility synergy and strain hardening capacity in the laser-treated samples. This mechanism could effectively facilitate resisting the initiation and propagation of the fatigue microcracks, which was further validated by the in-situ transmission electron microscope observations. Our results in this study could be further applied for the modification of grain morphology and precipitation distribution for additive manufacturing applications, critical to the development of advanced structural Mg alloys with high service performance in practical engineering environments.

High strength Al−Mg−Sc−Zr alloy with heterogeneous grain structure and intragranular precipitation produced by laser powder bed fusion

Development of a high strength Zr/Sc/Hf-modified Al-Mn-Mg alloy using Laser Powder Bed Fusion: Design of a heterogeneous microstructure incorporating synergistic multiple strengthening mechanisms

Microstructural Evaluation and Tensile Properties of Al-Mg-Sc-Zr Alloys Prepared by LPBF

Strong and ductile Al–Mn–Mg–Sc–Zr alloy achieved in fabrication-rate enhanced laser powder bed fusion

Achieving superior high-temperature mechanical properties in Al-Cu-Li-Sc-Zr alloy with nano-scale microstructure via laser additive manufacturing

Exploiting the rapid solidification potential of laser powder bed fusion in high strength and crack-free Al-Cu-Mg-Mn-Zr alloys

Novel isotropic mechanical properties of laser powder-bed fusion Sc/Zr modified Al alloy

Microstructure and mechanical properties of Al-Mg-Mn-Er-Zr alloys fabricated by laser powder bed fusion

Superior strength of laser-arc hybrid additive manufactured Al-Zn-Mg-Cu alloy enabled by a tunable microstructure

Laser powder bed fusion of Zr-modified Al–Cu–Mg alloy: Crack-inhibiting, grain refinement, and mechanical properties

Laser powder bed fusion of an age-hardenable Mg-10Gd-0.2Zr alloy with excellent strength-ductility synergy

Selective laser melting Al-3.4Mg-0.5Mn-0.8Sc-0.4Zr alloys: From melting pool to the microstructure and mechanical properties

Effect of Powder Spreading Parameters on Laser Absorption Behavior and Processability of High‐Strength Aluminum Alloy Fabricated by Laser Powder Bed Fusion

Developing a high-strength Al-Mg-Si-Sc-Zr alloy for selective laser melting: Crack-inhibiting and multiple strengthening mechanisms

Developing a novel lightweight Al–Mg–Li alloy for laser powder bed fusion additive manufacturing: Parameter optimization, microstructure evolution, and mechanical performance

Microstructure and mechanical properties of Al-Fe-Sc-Zr alloy additively manufactured by selective laser melting

Microstructural Evolution of a High-Strength Zr-Ti-Modified 2139 Aluminum Alloy for Laser Powder Bed Fusion

Superior strength-ductility synergy and fatigue resistance of heterogeneous structured AZ41 Mg alloy by laser surface processing

High strength Al–Li alloy development for laser powder bed fusion

Temperature gradient induced tough-brittle transition behavior of a high-strength Al-4.2Mg-0.4Sc-0.2Zr alloy fabricated by laser powder bed fusion additive manufacturing

Selective Laser Melting of Gas Atomized Al–3.02Mg–0.2Sc–0.1Zr Alloy Powder: Microstructure and Mechanical Properties