Abstract:The need for 2219 aluminum alloy and 2195 Al–Li alloy dissimilar friction stir welding (FSW) arises as the conventional 2219Al alloy was gradually replaced by the novel 2195Al alloy in fabrication of fuel tanks. However, the systematic investigation about the effect of welding parameters and material positioning on the microstructure evolution and mechanical properties of dissimilar FSW 2219Al/2195Al joints is lacking. In the present study, 2219Al-T8/2195Al-T8 plates were subjected to FSW under rotation rates of 800–1200 rpm and welding speeds of 200–800 mm min −1 with placing 2219Al-T8 alloys on the advancing side (AS) and retreating side (RS), respectively. The results showed that sound FSW joints were obtained under all the welding conditions. Welding parameters and material positioning affected the joint strength and fracture failure behavior. The FSW thermal cycle resulted in low hardness zones (LHZs) on both the 2219Al-T8 and 2195Al-T8 sides. The LHZ on the 2219Al-T8 side, characterized by partial coarsening of θ ′ (Al 2 Cu) precipitates and dissolution of the residual precipitates, showed the minimum hardness in the entire FSW joints. When 2219Al-T8 alloy was placed on the AS, the LHZ on the 2219Al-T8 side experienced higher peak temperature, and therefore more dissolution of θ ′ than that on the RS, thereby obtaining higher tensile strength. The tensile strength of the FSW joints at room temperature and − 196 °C largely increased as the welding speed increased from 200 to 400 mm min −1 . The FSW joints presented much higher tensile strength at − 196 °C than that at room temperature under the identical welding parameters and material position. The FSW joints fractured along the LHZ on the 2219Al-T8 side during tension. For the bending testing, the up and down bending failure angles were about 91–117° and 88–109°, respectively, with the weak zone appearing in "S" line or HAZ on the 2195Al-T8 side.

Experimental and Numerical Investigation of Mechanical Properties and Stress Intensity Factor of Dissimilar Spot Weld Joints

Assessing the Residual Stresses in Dissimilar Welded Joint: Depth-Sensing Indentation Testing and Numerical Simulation

Numerical and experimental study of the hot cracking phenomena in 6061/7075 dissimilar aluminum alloy resistance spot welding

Experimental Investigation and Characterization of Friction Stir Spot-Welded Dissimilar Aluminum Copper Metallic Lap Joints

Modeling and Experimental Investigation of the Impact of the Hemispherical Tool on Heat Generation and Tensile Properties of Dissimilar Friction Stir Welded AA5083 and AA7075 Al Alloys

Optimization of friction stir spot welding process parameters for Al-Cu dissimilar joints using the energy of the vibration signals

Experimental investigation on friction stir welding of dissimilar aluminium alloys

Investigation on the mechanical properties and microstructural analysis of dissimilar friction stir welding of AA5154/AA7150

Dissimilar Friction Stir Welds in AA2219-AA5083 Aluminium Alloys: Effect of Process Parameters on Material Inter-Mixing, Defect Formation, and Mechanical Properties

Experimental Investigation of Material Properties in FSW Dissimilar Aluminum-Steel Lap Joints

On the investigation of microstructure and mechanical properties of the AlCoCrFeNi 2.1 /316 L dissimilar spot-welded joint

Combined numerical and experimental estimation of the fracture toughness and failure analysis of single lap shear test for dissimilar welds

Investigations on mechanical features and mechanical performance of rotary friction welded Al-Cu joint at optimized conditions

On the Investigation of Microstructure and Mechanical Properties of the AlCoCrFeNi2.1/316 L Dissimilar Spot-Welded Joint

Effects of material combination for ultrasonic spot welding on microstructure and strength of Al/Al, Al/Cu, and Al/Ni dissimilar joints

Microstructure and XRD Analysis of FSW Joints for Copper T2/aluminium 5A06 Dissimilar Materials

Experimental investigation and optimization of mechanical properties on combination of higher and lower strength of aluminum alloys

Mechanical Properties and Fracture Behavior of the Refill Friction Stir Spot Welding Dissimilar Aluminum Alloy Joints

An experimental study and parameter optimization of FSW for welding dissimilar 6061 and 7075 Al alloys

Experimental Study on Mechanical Behaviour of Friction Stir Welded Aluminium Alloy Butt Joints

Dissimilar friction stir welding of 2219-T8 and 2195-T8 aluminum alloys: part I—microstructure evolution and mechanical properties