Abstract:In this investigation the effect of various spatial hardness gradients (e.g. linear and nonlinear) on rolling contact fatigue (RCF) life are examined through a Mises-based plasticity framework. The plasticity framework, which utilizes kinematic hardening was embedded into a finite element (FE) model, which utilized continuum damage mechanics (CDM) to facilitate life calculations by simulating material deterioration as a function of cycle. CDM critical parameters – elastic damage law resistance stress (σr), elastic damage rate exponent (m), plastic damage law resistance stress (S0), plastic damage rate exponent (q) – were established from open literature experimental torsion stress-life data. A parametric study was then performed to quantify the relation between RCF life and (1) type of spatial gradient (e.g. linear, polynomial degree 4, polynomial degree 0.25), (2) depth of spatial gradient normalized with respect to half-contact width (e.g. 1b, 2.5b, 5b, 10b), (3) magnitude of residual stress, and (4) contact pressure. Additionally, FE simulations were conducted on non-graded, or uniform hardness microstructures and used to compare to the results from the parametric study. The RCF results indicated that polynomial gradients with degree greater than 1 outperform linear and polynomial gradients with degree less than 1, with differences between gradient types more apparent at shallower gradient depths. RCF resistance is improved with increasing gradient depth and increasing compressive residual stress. Regression analysis of the results from this investigation yielded a fatigue life expression that was formed as a function of the 4 input variables, with life improvement factors comparing well with experimental data from the open literature.

A crystal plasticity framework for modelling the rolling contact fatigue of planetary roller screw mechanism

Modelling micropit formation in rolling contact fatigue of bearings with a crystal plasticity damage theory coupled with cohesive finite elements

Multi-scale modelling of the thermally coupled planetary roller screw mechanism with curved fractal contact

Crystal plasticity modeling of grain boundary softening and fatigue in U75V pearlite steel under low strain conditions: A study of cyclic rolling contact fatigue

The effect of friction on surface crack initiation in rolling contact fatigue considering damage accumulation

On the effect of microplasticity on crack initiation from subsurface defects in rolling contact fatigue

A peridynamic damage-cumulative model for rolling contact fatigue

Micromechanism of Plastic Accumulation and Damage Initiation in Bearing Steels under Cyclic Shear Deformation: A Molecular Dynamics Study

Effect of spatial hardness distribution in rolling contact fatigue performance of bearing contacts

A Multiscale Accuracy Degradation Prediction Method of Planetary Roller Screw Mechanism Based on Fractal Theory Considering Thread Surface Roughness

Mesoscopic coupled plasticity-damage model of rough surface considering size-dependent plasticity

Research on Fractal Model of Load Distribution and Axial Stiffness of Planetary Roller Screw Mechanism Considering Surface Roughness and Friction Factor

A micromechanics-based machine learning model for evaluating the microstructure-dependent rolling contact fatigue performance of a martensitic steel

Crystal plasticity theory coupled with meso-damage to predict the ratchetting behavior of nickel-based single crystal superalloy

Accumulated crystal plasticity dissipation energy driven continuum damage two-scale model for fretting fatigue initiation life

Microstructure-informed, predictive crystal plasticity finite element model of fatigue-dwells

Numerical analysis of rolling contact fatigue crack initiation Considering material microstructure

Experimental and crystal plasticity modelling study on the crack initiation in micro-texture regions of Ti-6Al-4V during high cycle fatigue tests

Study on predicting rolling contact fatigue of pitch bearing raceway in offshore wind turbine

A peridynamic study on the effects of surface topography on rolling contact fatigue

Research on Rolling Contact Fatigue Failure of the Bearing Used in High-Speed Electric Multiple Units’ Axle Box Based on a Damage-Coupled Elastic–Plastic Constitutive Model