Abstract:A high-temperature, high-cycle fatigue test was conducted on a nickel-based single-crystal superalloy with a pore structure. Optical and scanning electron microscopy were utilized to examine the crack propagation paths and fatigue fracture surfaces at the macro and micro scales. The analysis of crack initiation and propagation related to the pore structure facilitated the development of a crack shape factor reflecting these distinct fracture behaviors. Predictions about the high-cycle fatigue stress experienced by the specimen were made, accompanied by an error analysis, providing critical insights for precise stress calculations and structural optimization in engine blade design. The results reveal that high-cycle fatigue cracks originate from corner cracks at pore edges, with the initial propagation displaying smooth crystallographic plane features. Subsequent stages show clear fatigue arc patterns in the propagation zones. The fracture surface exhibits the significant layering of oxide layers, primarily composed of NiO, with traces of CoO displaying columnar growth. AL2O3 is predominantly found at the interfaces between the matrix and oxide layers. Short and straight dislocations near the oxide layers and within the matrix suggest that dislocation multiplication and planar slip dominate the slip mechanisms in this alloy. The orientation of the fracture surface is mainly perpendicular to the load direction, with minor inclined facets in localized areas. Correlations were established between the plastic zone dimensions at the crack tips and the corresponding fatigue stresses. Without grain boundaries in single-crystal alloys, these dimensions are easily derived as parameters for fatigue stress analysis. The selected crack shape factor, "elliptical corner crack at pore edges", captures the initiation and propagation traits relevant to porous structures. Subsequent calculations, accounting for the impact of oxide layers on stress assessments, indicated an error ratio ranging from 1.00 to 1.21 compared to nominal stress values.

Crystal plasticity theory coupled with meso-damage to predict the ratchetting behavior of nickel-based single crystal superalloy

Meso-scale low-cycle fatigue damage of polycrystalline nickel-based alloy by crystal plasticity finite element method

Anisotropic Thermomechanical Fatigue of a Nickel-Base Single-Crystal Superalloy Part I: Effects of Crystal Orientations and Damage Mechanisms

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Influence of crystal orientations on the creep fracture of a nickel-based single crystal superalloy

Crystal plasticity modeling of low-cycle fatigue behavior of an Mg-3Al-1Zn alloy based on a model, including twinning and detwinning mechanisms

Crystal plasticity constitutive model and thermodynamics informed creep-fatigue life prediction model for Ni-based single crystal superalloy

Grinding subsurface damage mechanism of nickel-based single crystal superalloy based on stress-strain

Cyclic-loading microstructure-property relations from a mesoscale perspective: An example of single crystal Nickel-based superalloys

A modified damage-coupled viscoplastic constitutive model for capturing the asymmetric behavior of a nickel-based superalloy under wide creep-fatigue loadings

Life Assessment of Anisotropic Low Cycle Fatigue of Nickel-Base Single Crystal Superalloy

In-situ fatigue behavior study of a nickel-based single-crystal superalloy with different orientations

Crystallographic analysis on small fatigue crack propagation behaviour of a nickel‐based single crystal superalloy

Microscopic heterogeneity of low cyclic fatigue damage in Ni-based single crystal superalloy DD413

Uniaxial ratcheting and fatigue failure of tempered 42CrMo steel: Damage evolution and damage-coupled visco-plastic constitutive model

High-Cycle Fatigue Fracture Behavior and Stress Prediction of Ni-Based Single-Crystal Superalloy with Film Cooling Hole Drilled Using Femtosecond Laser

Geometric discontinuity effect on creep-fatigue behaviors in a nickel-based superalloy hole structure considering ratcheting deformation

Crystal Plasticity Modeling and Analysis for the Transition from Intergranular to Transgranular Failure in Nickel-based Alloy Inconel 740H at Elevated Temperature

A Damage-Effect-involved Phenomenological Crystal Plasticity Model and Computational Methods for Mechanical Responses of FeCrAl Alloys

Micro-strain and cyclic slip accumulation in a polycrystalline nickel-based superalloy

Creep-fatigue damage mechanisms and life prediction based on crystal plasticity combined with grain boundary cavity model in a nickel-based superalloy at 650°C