Abstract:Grain boundaries (GBs) of metallic materials will become the weakest and most vulnerable place when the materials deform at high temperature. This could directly affect deformation flow, plastic strengthening, the initiation and propagation of microcracks, and finally the fracture failure of materials. In this research, to reveal the high temperature deformation mechanisms of twinning–induced plasticity (TWIP) steels, the crystal plasticity finite element method (CPFEM) was employed to model the mechanical response of grain interiors. The cohesive zone model (CZM) of the bi–linear traction separation law (TSL) was developed to describe the damage and failure of GBs. By combining CZM and CPFEM, an analysis method was proposed to investigate the effect of the microstructure morphology, orientation and size of grains, and temperature. Furthermore, the damage initiation, accumulation and fracture at GBs were represented by the representative volume element model based on the CZM–CPFE method to explore the influences of GB angle, grain size and local microvoids (including the location and size) on the GB cracking. The stress damage cloud maps, the distribution of quadratic stress damage initiation criterion (QUADSCRT) and the scalar stiffness degradation (SDEG) describing the damage and fracture along the GBs were used to articulate the relationships of GB angle, size effect, local microvoids and the expected failure strain. The results show that low angle grain boundaries (LAGBs), the small average grain size (<21.2 μm), microvoids at the horizontal GBs and microvoids with a diameter below 1.5 μm can delay the initiation of microcracks and fracture failure along the GBs. The predicted damage and failure of GBs and the intergranular cracking characteristics in plastic deformation of TWIP steels at high temperature were corroborated by microscopic in–situ SEM experiments, in which the deformation characteristics inside the grains, and microcrack initiation and propagation near GBs were observed at 500 and 750°C. This research enhances the understanding of intergranular fracture, mechanical response and microstructure evolution of TWIP steels worked at different temperatures, and also provides a new way and strategy for studying the deformation behaviours of TWIP steels considering GB properties.

Crystal Plasticity Modeling and Analysis for the Transition from Intergranular to Transgranular Failure in Nickel-based Alloy Inconel 740H at Elevated Temperature

Cyclic Plasticity Modeling of Nickel-Based Superalloy Inconel 718 under Multi-Axial Thermo-Mechanical Fatigue Loading Conditions

Microcrack Nucleation and Propagation Investigation of Inconel 740H Alloy under in Situ High Temperature Tensile Test

In-situ Study of the Effect of Grain Boundary Misorientation on Plastic Deformation of Inconel 718 at High Temperature

Effect of Grain Size on Deformation and Fracture of Inconel718: an In-Situ SEM-EBSD-DIC Investigation

Research on microplastic deformation of Inconel718 under the conditions of high temperature and high strain rate

Studies of High-Temperature Fatigue Behavior and Mechanism for Nickel-Based Superalloy Inconel 625

Creep-fatigue damage mechanisms and life prediction based on crystal plasticity combined with grain boundary cavity model in a nickel-based superalloy at 650°C

Investigation of the fatigue damage mechanism of Inconel 617 at elevated temperatures obtained by in situ SEM fatigue tests

In-situ SEM study of temperature-dependent tensile behavior of Inconel 718 superalloy

In-situ study of adjacent grains slip transfer of Inconel 718 during tensile process at high temperature

Creep Performance Study of Inconel 740H Weldment Based on Microstructural Deformation Mechanisms

A Mechanism for the Evolution of Hot Compression Cracking in Inconel 625 Alloy Ingot With Respect to Grain Growth

Microstructure Evolution and Mechanical Properties of Inconel 740H During Aging at 750 °C

A unified material model for multiaxial ductile fracture and extremely low cycle fatigue of Inconel 718

Crystal plasticity simulation of the effect of grain size on the fatigue behavior of polycrystalline Inconel 718

Multi-Scale Crystal Plasticity Model of Creep Responses in Nickel-Based Superalloys

Cyclic microstructure analysis, crack propagation and life prediction of Inconel 750H considering the slip fracture energy

Temperature dependence of deformation behavior, microstructure evolution and fracture mechanism of Inconel 625 superalloy

Crystal plasticity modeling of non-Schmid yield behavior: from Ni3Al single crystals to Ni-based superalloys

Modelling of the intergranular fracture of TWIP steels working at high temperature by using CZM–CPFE method