Abstract:This study could present the size and morphology of two synthesized nanoparticles (NPs) by observing their smallest possible dimensions. Lanthanum carbonate nanoparticles were synthesized by sonochemical method through the interaction of lanthanum acetate hydrate and sodium carbonate in an aqueous medium with a probe sonicator. After rigorous washing followed by drying, the La 2 (CO 3 ) 3 ·8H 2 O(S1) NPs were calcined at a temperature of 600 °C to obtain lanthanum oxide nanoparticles (S2). Both NPs were characterised through various instrumental techniques. PXRD study showed orthorhombic with space group of Pccn (56) and hexagonal phases with space group of P 3 ̅ m 1 (164) for S1 and S2 respectively whose morphology and elemental analysis were studied through FESEM and EDX. High resolution TEM image of La 2 (CO 3 ) 3 ·8H 2 O and La 2 O 3 showed spherical shapes of the nanoparticles. Further study of XPS and FTIR conveyed detailed information of both nanoparticles whose TGA-DSC showed three step decomposition curves. The size and morphology of the synthesized nanoparticles have been found to have a distinct morphology and are found comparatively smaller in size than those observed in the earlier reported works (Table 1 Comparative study of synthesized lanthanum carbonate and lanthanum oxide NPs with various techniques applied by other researchers.

Facile synthesis of lanthanum carbonate octahydrate and lanthanum oxide nanoparticles by sonochemical method: systematic characterizations

Solvothermal Synthesis of Flower‐like Lanthanum Tartrate and Lanthanum Oxide Microspheres in Ethanol‐water Mixed System

Synthesis of lanthanum oxalate hierarchical micro-particles and nano-tubes

Direct Syntheses of Mixed Ion and Electronic Conductors La<sub>4</sub>Ni<sub>3</sub>O<sub>10</sub>and La<sub>3</sub>Ni<sub>2</sub>O<sub>7</sub>from Nanosized Coprecipitates

Effect of La-Introduced Manner on the Phase Formation and Morphology of the Hydrothermally Synthesized Pb_(0.70)La_(0.30)TiO_3 Powders

Facile green synthesis of lanthanum oxide nanoparticles: their photocatalytic and electrochemical applications

Sonochemical synthesis of nanocrystalline LaFeO3

Synthesis of Ultrafine Lanthanum Hydroxide Nanorods by A Simple Hydrothermal Process

Preparation of nano-sized lanthanum oxide by ultrasonic-homogeneous precipitation method

Hydrothermally synthesized Pb0.70La0.30TiO3 powders

Controllable Syntheses of Hexagonal and Lamellar Mesostructured Lanthanum Oxide

Facile synthesis of size-tunable lanthanum phosphate nanocrystals monodispersible in both organic and aqueous solutions

Time‐Dependent Hydrothermal Synthesis of La2O3 NPs for Effective Catalytic Activity of Ionic Dye

Low-temperature polymer precursor-based synthesis of nanocrystalline particles of lanthanum calcium manganese oxide (La_0.67Ca_0.33MnO_3) with enhanced ferromagnetic transition temperature

Hydrothermal synthesis, sintering behavior and oxide ionic conductivity of Na-doped lanthanum silicate

One-step synthesis and characterizations of cerium oxide nanoparticles in an ambient temperature via Co-precipitation method

Low-temperature chemical synthesis of lanthanum copper oxide

Facile Synthesis of La2Mo2O9 Nanoparticles Via an EDTA Complexing Approach

Process Optimization and Synthesis of Lanthanum-Cobalt Perovskite Type Nanoparticles (lacoo3) Prepared by Modified Proteic Method: Application of Response Surface Methodology

One-Pot Facile Synthesis and Optical Properties of Porous La2o2co3 Hollow Microspheres

Synthesis and luminescent properties of sub-5-nm lanthanide oxides nanoparticles