Abstract:In this work, a facile route using a simple solvothermal reaction and sequential heat treatment process to prepare 3D La2O3 flower-like nanostructures without employing templates or matrices for self-assembly is presented. The as-synthesized products were characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), energy dispersive X-ray spectroscopy (EDS), thermogravimetric analysis (TG), differential thermal analysis (DTA), and Fourier transformation IR (FTIR). SEM results demonstrate that the as-prepared flower-like precursor with average size of 5-7 mu m in diameter is composed of numerous nanoplates with a thickness of about 100 nm. Influencing factors such as solvothermal reaction temperature, surfactants, reaction time, and solvents were systematically investigated. 3D flower-like La2O3 nanostructures with many holes on the petals were obtained after calcinations of the flower-like precursor at 800 degrees C for 4 h. The BET surface area of the flower-like La2O3 nanostructures is 9.98 m(2)/g. Eu3+ doped flower-like La2O3 nanostructures were also prepared employing the same preparation process. The flower-like La2O3:Eu3+ nanostructures show a strong red emission corresponding to D-5(0)-F-7(2) transition (625 nm) of Eu3+ under ultraviolet excitation (267 nm). The possible formation mechanism for the 3D flower-like precursor was briefly discussed.

Solvothermal Synthesis of Flower‐like Lanthanum Tartrate and Lanthanum Oxide Microspheres in Ethanol‐water Mixed System

A Simple Solvothermal Process to Synthesize CaTiO3 Microspheres and Its Photocatalytic Properties

Solvothermal synthesis, characterization and formation mechanism of single-crystalline SrTiO3 dense spheres with monoethanolamine as reaction medium solvent

Synthesis of Highly Dispersed Barium Titanate Nanoparticles by a Novel Solvothermal Method

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Synthesis of lanthanum oxalate hierarchical micro-particles and nano-tubes

Synthesis of Ultrafine Lanthanum Hydroxide Nanorods by A Simple Hydrothermal Process

Solvent-controlled Synthesis of Three-Dimensional TiO2 Nanostructures Via a One-Step Solvothermal Route

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

Effects of the Volume Ratio of Water and Ethanol on Morphosynthesis and Photocatalytic Activity of CaTiO3 by a Solvothermal Process

Hydrothermal synthesis and characterization of core/shell ALOOH microspheres

Synthesis and Characterization of Mesoporous SrTiO3 Spheres Via a Poly Vinyl Alcohol‐Assisted Hydrothermal Route

Controllable Syntheses of Hexagonal and Lamellar Mesostructured Lanthanum Oxide

Effect of solvents on morphology and size of US nanoparticles via a solvothermal route

Preparation and Characterization of 3d Flower-Like La2o3 Nanostructures

Solvent-controlled synthesis and photocatalytic activity of hollow TiO2 microspheres prepared by the solvothermal method

A facile flame assisted approach to fabricate Ta2O5 microspheres

Effect of Solvents and Reaction Parameters on the Morphology of Ta2O5 and Photocatalytic Activity

Systematic Synthesis of Lanthanide Phosphate Nanocrystals

Solvothermal synthesis and luminescence of nearly monodisperse LnVO 4 nanoparticles

Solvothermal Synthesis of Hierarchical Eu2o3 Nanostructures Templated by Ps-B-Pmaa: Morphology Control Via Simple Variation of Water Contents