Effects of the atmosphere on the high tensile strength and robust flexibility of Lu2O3 fibrous membrane

Yongshuai Xie,Ying Peng,Lin Wang,Dehua Ma,Nan Wang,Luyi Zhu,Jian Zhang,Zhitai Jia,Xinqiang Wang,Guanghui Zhang

DOI: https://doi.org/10.1016/j.ceramint.2020.11.202

IF: 5.532

2021-03-01

Ceramics International

Abstract:We obtained Lu2O3 fibrous membrane, with robust flexibility and high tensile strength, by electrospinning a novel high lutetium content precursor. We observed the microstructure of the membrane and studied the mechanism of the heat-treated atmosphere and temperature on the mechanical properties of the membranes. The results showed that the Lu2O3 content in the precursor was 63%, and the decomposition temperature range of organic matter was wide. Heat treatment in nitrogen retained a small amount of residual carbon in the membrane. A small amount of carbon hindered the mass transfer process, increased the grain boundary density, inhibited the growth of crystal grains, and improved the tensile strength and flexibility of the fibrous membrane. The tensile strength of the Lu2O3 fibrous membrane was as high as 6.81 MPa after heat treatment at 1000 °C for 2 h, which was significantly higher than the reported ceramic fibrous membrane.

materials science, ceramics