Abstract:Abstract Nickel-based alloy coatings were widely used for the remanufacturing of dies and moulds by laser cladding, but the crack sensitivity would be increase due to the higher strength and hardness, which reduced the wear resistance of Ni-based alloys. In this paper, Ni-based coatings with the addition of a plastic phase (an austenitic stainless net) were prepared using laser cladding technology, and the CeO 2 was added in cladding layers. The cracking mechanism, microhardness, microstructure, phase composition, and wear properties were investigated. The relationship between thermal stress and the elastic and plastic fracture had been developed from the standpoint of fracture mechanics and thermal elastic fracture mechanics. The fracture criterion of the nickel-based coating was obtained, and the study has shown that the crack sensitivity could be reduced by decreasing the thermal expansion coefficient Δ α . Thus, a new method was proposed, which the stainless steel nets were prefabricated on the substrate. It was found that the number of cracks reduced significantly with the addition of stainless steel net. When the stainless steel net with 14 mesh was added in Ni-based coatings, the average microhardness of nickel composite coating was 565 HV 0.2 , which was 2.6 times higher than that of the 45 steel substrate. Although the rare earth oxide 4 wt.% CeO 2 and stainless steel net were added in the Ni-based coating reducing the microhardness (the average microhardness is 425 HV 0.2 ), the wear resistance of it improved substantially. The wear volume of Ni-based composite coating was 0.56×10 −5 mm 3 ·N −1 ·m −1 , which was 85.1% lower than that of 45 steel. The experiment results have shown that the Nickel-based composite coating is equipped with low crack sensitivity and high abrasive resistance with austenitic stainless net and the rare earth oxide 4 wt.% CeO 2 . This research offers an efficient solution to produce components with low crack susceptibility and high wear-resistance coatings fabricated by laser cladding.

A review on cracking mechanism and suppression strategy of nickel-based superalloys during laser cladding

Crack Formation Mechanisms and Control Methods of Laser Cladding Coatings: A Review

A Novel Grain Refinement Design to Inhibit Liquation Cracking in Laser Cladding Non-Weldable Nickel-Based Alloy

The role of shot peening on liquation cracking in laser cladding of K447A nickel superalloy powders over its non-weldable cast structure

Hot Crack Formation Mechanism and Inhibition of a Novel Cobalt-Based Alloy Coating during Laser Cladding

Study of Cracking Mechanism and Wear Resistance in Laser Cladding Coating of Ni-based Alloy

A comprehensive review of microstructural heterogeneities in the laser powder bed fusion of nickel-base superalloys with high γ′ content

Origin of hot cracking formation and suppression method in laser additive manufactured nickel-based superalloys

Effect of the Laser Cladding Parameters on the Crack Formation and Microstructure during Nickel Superalloy Gas Turbine Engines Repair

Experimental Research on Cracking Behavior During High-Power CO 2 Laser Cladding

The role of the pulsed-wave laser characteristics on restraining hot cracking in laser cladding non-weldable nickel-based superalloy

Laser cladding repairing of directionally solidified nickel base superalloy and its tensile properties

Dynamic evolution behavior of cracks for single-track and multi-track clads in laser cladding

A Study on the Cracking Behaviour in Laser Metal Deposition of IC10 Directionally Solidified Nickel-Based Superalloy

Crack Inhibition and Performance Modification of NiCoCr-Based Superalloy with Y2O3 Nanoparticles by Laser Metal Deposition

Recent Research Progress in the Mechanism and Suppression of Fusion Welding-Induced Liquation Cracking of Nickel Based Superalloys

Effects of Thermal Stress on the Formation and Cracking Behavior of Nickel-Based Superalloys by Selective Laser Melting Based on a Coupled Thermo-Mechanical Model

Crack initiation and propagation within nickel-based high-temperature alloys during laser-based directed energy deposition: A review

Evolution behavior of liquid film in the heat-affected zone of laser cladding non-weldable nickel-based superalloy

Research and progress of laser cladding on engineering alloys: A review

Research status on the effect of energy density on the forming microstructure and properties of nickel-based superalloys for laser additive manufacturing