Wet H2S corrosion and degradation of pipeline in amine regeneration system

Juliusz Orlikowski,Maciej Kalinowski,Igor Lasota,Piotr Maruszewski,Michal Szocinski,Kazimierz Darowicki
DOI: https://doi.org/10.1002/maco.202314252
2024-02-04
Materials and Corrosion
Abstract:Any material failure in refinery and petrochemical plants is associated with health and environmental hazard as well as considerable financial losses due to periodic shutdowns for repair. Identification of the failure causes is crucial from the damage prevention standpoint. In the paper, the authors investigate the case of wet H2S corrosion of a pipeline in amine regeneration system, correlating the material degradation with process parameters of the installation. The paper presents the results of non‐destructive testing examinations, metallographic tests and risk assessment of degradation related to corrosion of amine regeneration unit in a desulphurisation system. Intensive corrosion resulting from acid gases environment upon water condensation causes perforation of the pipeline. Detailed analysis reveals cracking related to the mechanism of wet H2S. Hydrogen penetration, resulting from the wet H2S process, causes a decrease in mechanical properties of steel and an increase in hydrogen content inside steel. Corrosion results mostly from high stream velocity, the presence of acid gases (with high ammonia content), the presence of amine and low stream temperature.
materials science, multidisciplinary,metallurgy & metallurgical engineering
What problem does this paper attempt to address?