Kinetic analysis of resin binder for casting in combustion decomposition process

Peng Wan,Jianxin Zhou,Yuancai Li,Yajun Yin,Xin Peng,Xiaoyuan Ji,Xu Shen

DOI: https://doi.org/10.1007/s10973-021-10902-3

IF: 4.755

2021-07-10

Journal of Thermal Analysis and Calorimetry

Abstract:<p class="a-plus-plus">Random stacking of waste foundry sand will cause great environmental pollution, so it is necessary to recycle the waste foundry sand produced by resin-bonded sand technology by hot-reclamation to eliminate the residual resin on its surface. The study of thermodynamics analysis of resin binder for casting in combustion decomposition process can provide theoretical support for thermal reclamation. In this paper, TG–DTA technology was applied to measure TG, TGA, DTG curves of the three kinds of resin binders at 0–800 °C (furan resin binder, phenolic urethane resin binder and alkaline phenolic resin binder). The ignition point, reaction peak temperature, activation energy, mode function and other parameters of the three resin binders were calculated by the curves, and conclusions are as follows: (1) Furan resin binder, phenolic urethane resin binder and alkaline phenolic resin binder were heated to 800 °C in air at a heating rate of 15 °C min<sup class="a-plus-plus">−1</sup>, and their residual mass was 9.8%, 2.7% and 33.7%, respectively; (2) the highest activation energy of furan resin binder, phenolic urethane resin binder and alkaline phenolic resin binder was 82.35 kJ mol<sup class="a-plus-plus">−1</sup>, 90.77 kJ mol<sup class="a-plus-plus">−1</sup> and 335.77 kJ mol<sup class="a-plus-plus">−1</sup>, respectively; (3) the reaction mode of three resin binders in each stage is Acceleratory α-time(<em class="a-plus-plus">n</em> = 1), f(α) = α, G(α) = lnα.</p>

chemistry, physical, analytical,thermodynamics