Abstract:To predict brittle fracture in high-strength steels, this study introduces a methodology for analyzing hydrogen-assisted degradation. The proposed approach considers the fully coupled problems of deformation-hydrogen diffusion and cohesive zone modeling. The analysis of hydrogen diffusion assumes that trapped and lattice hydrogen remain in a equilibrium state while accounting for the relationships between the increase in trap sites and plastic strain. The diffusion model simulates hydrogen diffusion in the small scale yielding (SSY) configuration at a crack tip. The simulation results reveal that hydrogen diffusion follows the hydrostatic stress distribution around the crack tip region. Additionally, the plastic strain near this area leads to an increased number of trap sites. Notably, the simulations indicate that lattice hydrogen is the dominant source of embrittlement when a sufficient amount of hydrogen atoms dissolve into the steel, as compared to trapped hydrogen. The hydrogen-assisted degradation evolution is studied by investigating the influence of hydrogen in a cohesive zone modeling (CZM) with a trapezoidal traction separation law (TSL), based on Hydrogen-Enhanced DEcohesion (HEDE) framework. The fully computational framework is utilized to simulate the hydrogen-charged fracture toughness test in a (CT) specimen made of 30CrMo high strength steel. It is demonstrated that the load bearing capacity of the specimen decreases with an increase in the initial hydrogen concentration. Furthermore, the study examines the evolution of the initial crack time with varying initial hydrogen concentrations. The initial hydrogen concentrations are estimated to match the maximum loads observed in the experimental load-displacement curves based on computational framework. The computational CTOD-R curves for hydrogen generally follow the experimental data, the marginally elevated computational CTOD values to underestimate the embrittling in hydrogen-contaminated steel. Overall, the present study proves the capability of this numerical technique to reproduce experimental findings related to hydrogen-assisted fracture.

Numerical Modeling for Hydrogen Permeation Through Steel Under Sour-Corrosion and Tensile Stress

Evaluation of corrosion morphology on mechanical properties of reinforcing steel bars using numerical simulation and simplified analytical model

Numerical analysis of the fully-coupled continuum cohesive modeling on the hydrogen-assisted degradation behavior in high-strength steel

Continuum Damage Model for Hydrogen Embrittlement in Ferritic Steels

Predictive Environmental Hydrogen Embrittlement on Fracture Toughness of Commercial Ferritic Steels with Hydrogen-Modified Fracture Strain Model

Experimental and Modeling Analysis of Hydrogen Motion Behavior in Welding Zone of 2.25Cr–1Mo–0.25 V Steel Welded Joint with Hydrogen Corrosion

Numerical Simulation of Steel Corrosion in Chloride Contaminated Concrete

Continuum Damage Mechanics Based Fatigue Life Prediction and Fatigue Property Analysis of Pitting Corrosion Steel Bars

Modeling of Hydrogen-Charged Notched Tensile Tests of an X70 Pipeline Steel with a Hydrogen-Informed Gurson Model

Modelling of hydrogen diffusion in a steel containing micro-porosity. Application to the permeation experiment

Finite element modeling of hydrogen atom diffusion and distribution at corrosion defect on aged pipelines transporting hydrogen

Molecular Dynamics Simulation of Reinforcing Steel Corrosion when Subjected to Both Chloride Attack and Mechanical Loading

Modelling Hydrogen Induced Stress Corrosion Cracking in Austenitic Stainless Steel

Fracture Strain Model for Hydrogen Embrittlement Based on Hydrogen Enhanced Localized Plasticity Mechanism

Modeling Corrosion Product Film Formation and Hydrogen Diffusion at the Crack Tip of Austenitic Stainless Steel

Numerical Simulation for Hydrogen-Assisted Cracking: An Explicit Phase-Field Formulation

A review of cohesive zone modelling as an approach for numerically assessing hydrogen embrittlement of steel structures

Understanding and mitigating hydrogen embrittlement of steels: a review of experimental, modelling and design progress from atomistic to continuum

Molecular‐Scale Modeling and Multiscale Experiments on the Elastic Properties of HR‐2 Steel Affected by Hydrogen

A Phase-field model for simulating hydrogen-induced pitting corrosion with solid-solid phase transformation in the metal

Modelling of hydrogen diffusion leading to embrittlement in austenitic stainless steels