Abstract:Coarse grain and poor thermal stability of Mg17Al12 are usually present in the as-cast Mg–Al alloys, which are detrimental to the mechanical properties. In this work, the microstructure evolution, and mechanical properties of as-cast AZ31-1Y alloy with different cooling rates (4.0–29.9 °C/s) were systematically investigated by thermal analysis and microstructure characterization. The results show that the addition of Y to AZ31 alloy results in the formation of primary Al2Y and eutectic Al2Y, while suppressing the formation of β-Mg17Al12. The AZ31-1Y alloy with a cooling rate of 29.9 °C/s exhibits the finest grain, with a grain refinement efficiency 40.9 % higher than that of AZ31 alloy with a cooling rate of 4.0 °C/s. After heat treatment, the acicular eutectic Al2Y is modified into a granular shape and numerous nano-sized Al2Y precipitates are observed within the α-Mg matrix. The addition of Y can effectively improve the mechanical properties of AZ31 alloy under high cooling rates, but the mechanical properties deteriorate at slower cooling rates due to stress concentration caused by the agglomeration of large-sized Al2Y particles. The optimal mechanical properties of the AZ31-1Y alloy are achieved at a cooling rate of 29.9 °C/s combined with subsequent heat treatment, and its YS, UTS, and EL reached up to 69 MPa, 293 MPa, and 14.5 %, respectively. Moreover, the related strengthening mechanisms are quantified. It is believed that this work can provide guidance for controlling the microstructure and optimizing the mechanical properties of as-cast Mg–Al alloys.

Study on the Fine Grain Size and Microhardness at the Interface of AZ31/Mg‐Y Composites

The Effect of Ti Particles Addition on the Microstructure and Mechanical Behavior of Mg AZ31/Al 6082 Composite Sheets

Enhancing the Mechanical Properties of Mg–Al Alloy by Introducing Al2Y Nanoparticles Via Rapid-Cooling Solidification and Optimized Heat Treatments

Effect of interfacial structure on grain refinement and strength of Ti particles reinforced AZ31 composites

Effect of Y addition on the interfacial microstructures and mechanical properties of C f /Mg composites

Microstructures and Mechanical Properties of Ultrafine-Grained Ti/AZ31 Magnesium Matrix Composite Prepared by Powder Metallurgy

Microstructure and Mechanical Properties of AZ31B Magnesium Alloy via Ultrasonic Surface Rolling Process

Microstructures And Mechanical Properties Of Nanocrystalline Az31 Magnesium Alloy Powders With Submicron Tib(2)Additions Prepared By Mechanical Milling

Microstructural Modification and Strength Enhancement by SiC Nanoparticles in AZ31 Magnesium Alloy During Hot Rolling

Effect of Y Content on Interfacial Microstructures and Mechanical Properties of C-F/Mg Composite

Interface microstructure and mechanical property of (Al2O3-SiO2)sf/AZ91D composite

Microstructural Evolution and Interfacial Characterization of Al18B4O33w/GWZ1031K Magnesium Matrix Composite During Heat Treatment

Enhancing grain refinement and mechanical properties of AA1100/MgAZ31/AA1100 composites by using different roll bonding techniques

Preliminary Investigations on the Mg–Al–Zn/Al Laminated Composite Fabricated by Equal Channel Angular Extrusion

Effect of grain size distribution and texture on the cold extrusion behavior and mechanical properties of AZ31 Mg alloy

Microstructures and the improved mechanical properties of AZ91 alloy by incorporating Ti-6Al-4V particles

Investigations on Microstructure, Mechanical Properties and Tribological Behavior of In-Situ Mg2Si Particles Reinforced AZ91 Composites

Grain Refining and Property Improvement of AZ31 Mg Alloy by Hot Rolling

Grain Refining of AZ31 Magnesium Alloy During Temperature-Differential Hot Rolling

Microstructure, mechanical properties and wear resistance of Ti particles reinforced AZ31 magnesium matrix composites

Microstructures and Mechanical Properties of Hot Rolled AZ31 Mg Alloy Sheets