Microstructure effects on the energy storage density in BiFeO3-based ferroelectric ceramics

Zhuo Yu,Jiangtao Zeng,Liaoying Zheng,Anthony Rousseau,Guorong Li,Abdelhadi Kassiba
DOI: https://doi.org/10.1016/j.ceramint.2021.01.133
IF: 5.532
2021-05-01
Ceramics International
Abstract:<p>Lead-free BiFeO<sub>3</sub>–BaTiO<sub>3</sub>–Bi(Mg<sub>2/3</sub>Nb<sub>1/3</sub>)O<sub>3</sub> (BFBT-BMN) ceramics with different grain sizes were fabricated by using a conventional solid-state reaction. The high-energy ball milling technique was utilized to obtain the fine-grained ceramics. The grain size reduction lowers the remanent polarization (<em>P</em><sub>r</sub>) and enhances the dielectric breakdown strength (<em>E</em><sub>b</sub>) leading to a drastic increase of the recoverable energy storage density (<em>W</em><sub>re</sub>). For the fine-grained BFBT-BMN ceramics, <em>W</em><sub>re</sub> greatly increases by 8 times from 0.16 J/cm<sup>3</sup> to 1.27 J/cm<sup>3</sup>, compared to the coarse-grained BFBT-BMN ceramics. Transmission electron microscopy (TEM) and piezo-response force microscopy (PFM) measurements revealed the occurrence of the polar nanoregions (PNRs) in the fine-grained BFBT-BMN ceramics. The dynamic and weakly correlated PNRs structure is responsible for the enhancement of recoverable energy storage density in the fined-grained BFBT-BMN ceramics. This work indicates that the grain size reduction is an effective way to modify the energy storage properties of BiFeO<sub>3</sub>-based ferroelectric ceramics.</p>
materials science, ceramics
What problem does this paper attempt to address?