Formation mechanism, dielectric properties, and energy-storage density in LiNbO3-doped Na0.47Bi0.47Ba0.06TiO3 ceramics

Qin Feng,Kai Huang,Nengneng Luo,Changlai Yuan,Changrong Zhou,Yuezhou Wei,Qingning Li,Toyohisa Fujita,Guohua Chen
DOI: https://doi.org/10.1007/s10854-020-03891-w
2020-07-06
Abstract:The development of ferroelectric (FE) ceramics with high recoverable energy-storage density (<i>W</i><sub>rec</sub>) critically affects the miniaturization and integration of advanced pulse-power capacitors. However, most lead-free FE materials have the shortcomings of large remanent polarization and low dielectric breakdown strength. In this work, a strategy of composition control was implemented to improve the <i>W</i><sub>rec</sub> of lead-free ceramics. The effects of Li and Nb ion incorporation on the structure, dielectric, and ferroelectric properties of the highly insulating (Na<sub>0.5</sub>Bi<sub>0.5</sub>)TiO<sub>3</sub>–BaTiO<sub>3</sub> (NBT–BT) ceramic was investigated. X-ray diffraction analysis of the samples revealed that the pure phase was isostructural to (Na<sub>0.5</sub>Bi<sub>0.5</sub>)TiO<sub>3</sub>. Dielectric measurements exhibited two pronounced anomalies which shift a certain angle within the depolarization-temperature range. The effects of LiNbO<sub>3</sub> content on the breakdown characteristics and discharge energy storage of NBT–BT ceramics were investigated. An enhanced discharged energy density of 1.05 J/cm<sup>3</sup>, calculated from a hysteresis loop, was observed at <i>x</i> = 4 mol%. The improved structure also resulted in an increase of up to 61% in breakdown strength.
What problem does this paper attempt to address?