Enhanced leaching of Mo by mechanically co-grinding and activating MoS2 with NaClO3 as an oxidizing additive

Yubiao Li,Qihang Xiao,Zhiming Li,Andrea R. Gerson

DOI: https://doi.org/10.1016/j.hydromet.2021.105625

IF: 4.217

2021-08-01

Hydrometallurgy

Abstract:<p>The slow leaching rate of molybdenite (MoS₂), due to its inert nature, and low recovery hinders the application of traditional hydrometallurgical processing. This study investigated the effects of grinding speed and time, molar ratio of sodium chlorate (NaClO₃, oxidant) to MoS₂, leaching time and temperature on the leaching efficiency of molybdenum (Mo). Grinding at low speeds via mechanical activation decreased particle size. However, at speeds over 450 rpm for 1.0 h, or at lower speeds but with longer time, it triggers a solid-state reaction (mechanochemistry) producing soluble Na₂Mo₂O₇. This may be due to the existence of an energy threshold for the solid-state reaction. The most suitable activating conditions were 600 rpm for 0.5 h, with a molar ratio of NaClO₃: MoS₂ = 5, leached in 0.1 M NaOH solution for 2.0 h at 348 K, giving rise to a Mo recovery of 74.8%. The initial acid leaching stage of the ground mixture is dominated by the dissolution of Na₂Mo₂O₇, giving rise to elevated Mo recovery. The later stage is controlled by the dissolution of MoS₂, slowing down the increase in Mo extraction. As compared to alkaline conditions, acidic leaching of MoS₂ ground at low speeds (non solid-state reaction) gives greater Mo recovery, due to the greater activity of NaClO₃ to MoS₂ under acidic conditions. However, the greatest Mo recovery is achieved in alkaline solution for MoS₂ ground at high speed (solid-state reaction) due to the occurrence of mechanochemical reaction.</p>

metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem this paper attempts to address is improving the leaching efficiency of molybdenum disulfide (MoS₂) in the hydrometallurgical process. Specifically, due to the inert nature of molybdenum disulfide, its leaching rate is slow and recovery rate is low, which limits the application of traditional hydrometallurgical processes. This study investigates methods to enhance the leaching of molybdenum disulfide through mechanical activation (i.e., co-grinding) and the use of sodium chlorate (NaClO₃) as an oxidizing additive. The focus of the research is to explore the effects of grinding speed, time, the molar ratio of sodium chlorate to molybdenum disulfide, leaching time, and temperature on the leaching efficiency of molybdenum (Mo).

The study found that at lower grinding speeds, mechanical activation primarily reduces particle size; however, when the grinding speed exceeds 450 revolutions per minute (rpm) for 1 hour, or when grinding time is extended at lower speeds, a solid-state reaction (mechanochemical reaction) is triggered, producing soluble Na₂Mo₂O₇. This phenomenon may be due to the existence of an energy threshold for the solid-state reaction. The optimal activation conditions are grinding at 600 rpm for 0.5 hours, with a molar ratio of sodium chlorate to molybdenum disulfide of 5, leaching in 0.1 M NaOH solution at 348 K for 2 hours, achieving a molybdenum recovery rate of 74.8%. The results indicate that through mechanical activation and mechanochemical reactions, the leaching efficiency of molybdenum disulfide can be significantly improved, providing a new strategy for molybdenum extraction.