Effect of mechanical activation on the hypochlorite leaching of Sarcheshmeh molybdenite concentrate
Reshad Hesami,Ali Ahmadi,Mohammad Raouf Hosseini,Masoumeh Torabi
DOI: https://doi.org/10.1080/01496395.2021.2018712
IF: 2.799
2022-01-05
Separation Science and Technology
Abstract:Hydrometallurgical extraction of molybdenum from sulfidic molybdenite concentrates is an important issue from technical, economic, and environmental viewpoints. The influence of mechanical activation on the hypochlorite leaching of a molybdenite concentrate (Kerman, Iran) were studied in a stirred reactor at batch mode. The effects of several critical parameters, including pH, temperature, reaction time, NaClO concentration, and liquid to solid (L/S) ratio on the rate and extent of molybdenum extraction from the concentrate were investigated. Maximum molybdenum extractions, 98% and 95%, obtained for the mechanically activated and nonactivated concentrates, respectively after 60 min at 50°C, stirring speed of 500 rpm, L/S of 333 mL/g, pH of 9, and using 40% NaClO solution. Specific surface area and particles size measurements in conjunction with FE-SEM images showed that improvement in the extraction after mechanical activation could be due to increasing the surface area and changing the crystal structure of the concentrate. Mechanical activation had a significant effect on molybdenum extraction after 2 min, (13% difference in extraction); however, after 60 min, molybdenum extractions from mechanically activated and nonactivated samples were 97% and 92%, respectively. It was found that mechanical activation has a significant effect on the leaching of molybdenite in short reaction times.
engineering, chemical,chemistry, multidisciplinary