Abstract:Transparent and conductive Ti-doped In2O3 (TIO)/Ag/Ti-doped In2O3 (TAT) multilayer films were deposited on colorless poly imide (CPI) substrates by direct current (DC) and radio frequency (RF) magnetron sputtering at room temperature. During deposition the thickness of both the top and bottom TIO layer was fixed at 30 nm, while the thickness of the Ag interlayer was varied, to 5, 10, and 15 nm, to enhance the optical, electrical and mechanical properties of the films. In the XRD analysis the TIO films did not show any characteristic peaks in the diffraction pattern. The 10 nm thick Ag inter layer showed some characteristic peaks of Ag (111), (200), (220) and (311), respectively, and the grain size of the Ag interlayer enlarged as Ag thickness increased. To investigate the most efficient Ag interlayer thickness, a figure of merit (FOM) based on the opto-electrical performance of the transparent conducting films was compared. The films with a 10 nm thick Ag interlayer exhibited a higher FOM of 1.71 × 10-2 Ω-1 than the other films. When the radius of the film's curvature was reduced to 1.7 mm, the TIO single layer films showed a 13 times increase in sheet resistance, while the TAT (30/10/30 nm) films showed an insignificant change in sheet resistance. From the observed results, it was concluded that the Ag interlayer in the TAT multilayer films enhanced the opto-electrical performance of the films and also acted as a potent bridge which assured the high flexibility endurance of the films.

Thickness-Dependent NIR LSPR of Curved Ag/TiS2 Bilayer Film

Size dependence of plasmon absorption of Ni nanoparticles embedded in BaTiO3/SrTiO3 superlattices

Plasmon Resonant Absorption And Third-Order Optical Nonlinearity In Ag-Ti Cosputtered Composite Films

Thickness-dependent surface plasmon resonance of ITO nanoparticles for ITO/In-Sn bilayer structure

Tunable Surface Plasmon Resonance Frequencies of Monodisperse Indium Tin Oxide Nanoparticles by Controlling Composition, Size, and Morphology

Large Range Localized Surface Plasmon Resonance of Ag Nanoparticles Films Dependent of Surface Morphology

Ito-Tin-Ito Sandwiches For Near-Infrared Plasmonic Materials

Effect of Ag layer thickness on optical and electrical properties of ion-beam-sputtered TiO2/Ag/TiO2 multilayer thin film

Analysis of Localized Surface Plasmon Resonance in Ag/ITO/CdS/SiO2 Multilayered Nanostructured Composite

Tuning the Refractive Index Sensitivity of LSPR Transducers Based on Nanocomposite Thin Films Composed of Noble Metal Nanoparticles Dispersed in TiO2

Controllable Modulation of Surface Plasmon Resonance Wavelength of ITO Thin Films

Study of Optical and Electrical Properties of TiO2/Ag/TiO2 Multilayers

Tunable near-infrared light emission from layered TiS3 nanoribbons

Microstructure and Optical Properties of Ag/Tio2 Multilayers

The Effect Of Underlayer Thin Films On The Surface-Enhanced Raman Scattering Response Of Ag Nanorod Substrates

Investigation of Surface Plasmon Resonance in Composite Nanostructure of Silver Film and Nanowire Array

Excitation of Surface Plasmon Resonance in Composite Structures Based on Single-Layer Superaligned Carbon Nanotube Films

The Study of Surface Plasmon Resonance in Au-Ag-Au Three-Layered Bimetallic Nanoshell: the Effect of Separate Ag Layer

Direct evidence of visible surface plasmon excitation in ITO film coated on LiNbO_3 slabs

Si Underlayer Induced Nano-Ablation In Aginsbte Thin Films

Influence of Ag interlayer Thickness on the Optical, Electrical and Mechanical Properties of Ti-doped In2O3/Ag/Ti-doped In2O3 Multilayer Flexible Transparent Conductive Electrode