Abstract:The present study investigates the selective oxidation of a 0.1C-6Mn-2Si medium-Mn advanced high-strength steel during austenization annealing heat treatments as a function of process atmosphere oxygen partial pressure and annealing time. It was determined that the surface oxide growth kinetics followed a parabolic rate law with the minimum rate belonging to the lowest oxygen partial pressure atmosphere at a dew point of 223 K (− 50 °C). The chemistry of the surface and subsurface oxides was studied using STEM + EELS on the sample cross sections, and it was found that the surface oxides formed under the 223 K (− 50 °C) dew-point atmosphere consisted of a layered configuration of SiO2, MnSiO3, and MnO, while in the case of the higher pO2 process atmospheres, only MnO was detected at the surface. Consistent with the Wagner calculations, it was shown that the transition to internal oxidation for Mn occurred under the 243 K (− 30 °C) and 278 K (+ 5 °C) dew-point atmospheres. However, the predictions of the external to internal oxidation for Si using the Wagner model did not correlate well with the experimental findings nor did the predictions of the Mataigne et al. model for multi-element alloys. Investigations of the internal oxide network at the grain boundaries revealed a multilayer oxide structure composed of amorphous SiO2 and crystalline MnSiO3, respectively, at the oxide core and outer shell. A mechanism for the formation of the oxide morphologies observed, based on kinetic and thermodynamic factors, was proposed. It is expected that only the fine and nodule-like MnO oxides formed on the surface of the samples annealed under the 278 K (+ 5 °C) dew-point process atmosphere for 60 and 120 seconds are sufficiently thin and of the desired dispersed morphology to promote reactive wetting by the molten galvanizing bath.

Identification of Surface Selective Oxides on Continuous Annealed Steels

High‐Temperature Oxidation of 60si2mn Spring Steel in Dry Air and Wet Air: Insights from an Experimental and First‐Principles Study

Surface Selective Oxide Reduction During the Intercritical Annealing of Medium Mn Steel

Thermodynamic Consideration on Selective Surface Oxidation of High Strength Steels Prior to Hot-Dip Galvanizing

Influence of Fe Oxidation on Selective Oxidation Behavior of Si and Mn Added in High Strength Sheet Steel

Characterization of surface layers of oxidation-reduction treated Si and Mn added advanced high strength steel

Raman Spectroscopic Analysis of the Reaction between Al-Si Coatings and Steel

Selective Oxidation of a 0.1C-6Mn-2Si Third Generation Advanced High-Strength Steel During Dew-Point Controlled Annealing

Effect of annealing process on surface selective oxidation behavior of C-Mn-Si high strength steels

Investigation of Thin Coatings from Mn-Co-Fe System Deposited by PVD on Metallic Interconnects for SOFC Applications

Surface analyses and depth profiles of oxide scales formed on alloy surface

A Study of the Oxide Layer on the Surface of a TiN Coating

Influence of Si Content on Selective Oxidation and Oxide Scale Phase Transition During Hot-Rolled Coiling

Insight into scale transformation and internal oxidation mechanism of hot rolled Si Mn added high strength steel

Study of Precipitates in Oxide Dispersion-Strengthened Steels by SANS, TEM, and APT

Surface characterization of plasma rotating electrode atomized 30CrMnSiNi2A steel powder

In Situ Full-Field Measurement of Surface Oxidation on Ni-based Alloy Using High Temperature Scanning Probe Microscopy.

Adsorption behavior of the surface conditioning agent particles on the surface of high-strength steel

Study of the surface oxides and corrosion behaviour of an equiatomic CoCrFeMnNi high entropy alloy by XPS and ToF-SIMS

XPS Studies on Composite TiO<sub>2</sub>-SiO<sub>2</sub> Thin Films Deposited on Metal Substrate by Sol-Gel

XPS studies on composite TiO2-SiO2 thin films deposited on metal substrate by sol-gel