Abstract:To improve the wear resistance of TC4 titanium alloy, two types of wear-resistant coatings were applied to the surface using laser melting: Ni60 + 50% WC and d22 powder priming. The phase composition and microstructure of the coatings were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM), and energy spectroscopy (EDS). The mechanical properties of the coating were tested using an HV-1000 micro-Vickers hardness tester, an HRS-2M high-speed reciprocating friction and wear tester, and a WDW-100D electronic universal testing machine. The results show that Ni60 + 50% WC composite coating and d22 priming + (Ni60 + 50% WC) composite coating mainly consist of W2C, TiC, Ni17W3, Ni3Ti, and TixW1−x phases. Compared to the TC4 substrate, the microhardness of both coatings is significantly higher, approximately 2.8 times the microhardness of the substrate. In frictional wear experiments, the average friction factors of the two coatings and the TC4 substrate are 0.476, 0.55, and 0.865, respectively, and the wear of the two coatings is only 0.0559–0.0769 that of the TC4 substrate, with a significant increase in wear resistance, nearly 17 times higher than that of the substrate. The coating shows flaking, shallow abrasion marks, and granular debris, dominated by adhesive wear and fatigue wear, while the TC4 substrate shows more furrows on the surface, dominated by abrasive wear. The shear bond strengths of the Ni60 + 50% WC composite coating and the d22 powder primed + (Ni60 + 50% WC) composite coating were 188.19 MPa and 49.11 MPa, respectively. Conclusion: both coatings significantly improve the hardness and wear resistance of the TC4 titanium alloy substrate surface, with the Ni60 + 50% WC composite coating performing better in hardness, wear resistance, and bond strength.

Study on the impact of laser power variation on the performance of Ti-6Al-4 V coating by laser cladding on HT250

Effect of laser power on microstructure and properties of Ti-Al/WC composite coatings

Study on fabrication of multi-phase reinforcement coatings on Ti6Al4V by laser cladding for enhanced tribological performance

Microstructure and Wear Resistance of Ti6Al4V Titanium Alloy Laser-Clad Ni60/WC Composite Coating

Microstructure and Mechanical Properties of a Ti-6Al-4V Titanium Alloy Subjected to Laser Cladding

Microstructure and wear properties of TiCN/Ti coatings on titanium alloy by laser cladding

Study on the effect of TiC/B on the performance of laser cladding in-situ fabricating wear-resistant self-lubricating coatings

Microstructure, High-Temperature Wear Resistance, and Corrosion Resistance of Laser Cladded Co-Based Coating

The Wear Behavior of the Laser Cladded Ti-Al-Si Composite Coatings on Ti-6Al-4V Alloy with Additional TiC

Effect of process parameters on the microstructure evolution and wear property of the laser cladding coatings on Ti-6Al-4V alloy

Microstructure and properties of pure titanium coating on Ti-6Al-4V alloy by laser cladding

Microstructure and wear resistance of laser-clad Ni60-Ti-B4C coatings

Microstructural and Performance Analysis of (TiAl)95−xCu5Nix Coatings Prepared via Laser Surface Cladding on Ti–6Al–4V Substrates

Study of the Performance of Laser Melting Wear-Resistant Coatings on TC4 Titanium Alloy Surfaces

Microstructure and properties of Ti–Al–C composite coatings prepared by laser cladding

Laser Synthesis of Titanium Aluminides Matrix Composite Coatings Reinforced by In-Situ Titanium Carbide Particles on Ti-6Al-4V Substrate

Development and Characterization of Laser Clad High Temperature Self-Lubricating Wear Resistant Composite Coatings on Ti–6Al–4V Alloy

Computational and Experimental Investigation of Micro-Hardness and Wear Resistance of Ni-Based Alloy and TiC Composite Coating Obtained by Laser Cladding

Investigation into corrosion and wear behaviors of laser-clad coatings on Ti6Al4V

Microstructure and wear resistance of laser cladding NiCrAlY/TC4 composite coatings with in-situ synthesized transition layer by modulating thermal boundary in nitrogen atmosphere

Microstructure and Wear Resistance of Ti5Si3/Ti3Al Composite Coatings Prepared by Laser Cladding on TA2 Titanium Alloy