Abstract:The present study investigated the effects of solution treatments on the microstructure and mechanical properties of Inconel 625 fabricated by electron beam freeform fabrication. The results indicated that the microstructure of the as-deposited specimen exhibited typical dendritic characteristics. Meanwhile, the Laves ((Ni,Fe,Cr)2(Nb,Mo,Ti)) phases and needle-shaped δ phases precipitated. The deposition process led to the development of a preferred orientation feature along the building direction, and the typical {001}<100> plate texture was observed. Solution treatments at 900 °C and 1000 °C resulted in the precipitation of more δ phases, and the volume fraction was approximately 5.29% and 7.96%, respectively. The precipitated phases fully dissolved at solution temperatures of 1100 °C and 1200 °C, and equiaxed grains with a twin substructure were formed. The recrystallization weakened the preferred orientation, leading to a decrease in grain size and the formation of {111}<1-10> texture. The as-deposited specimen exhibited an ultimate tensile strength (UTS) of 682 MPa, a yield strength (YS) of 410 MPa, and an elongation of 56.4%. Solution treatment had minimal impact on the UTS, and the YS was mainly contributed by the solid solution strengthening. However, the elongation was greatly improved at elevated solution temperatures, and the elongation was increased to 72.1% at most. The primary mode of fracture was toughness fracture, which was attributed to the coalescence of microvoids. The solution treatment at 900 °C led to a fracture pattern that exhibited a combination of toughness and brittleness, and decreased the elongation to 48.5%.

Microstructure and mechanical properties of Co-28Cr-6Mo-0.22C investment castings by current solution treatment

Effect of Solution Treatment on Microstructure and Mechanical Properties of As-Cast Al-12Si-4Cu-2Ni-0.8Mg-0.2Gd Alloy

Effects of Solution Treatment on the Microstructure, Tensile Properties, and Impact Toughness of an Al–5.0Mg–3.0Zn–1.0Cu Cast Alloy

Effects of solution treatment on microstructure and tensile properties of as-cast alloy 625

Effect of Solution Treatment on Microstructures and Mechanical Properties of Centrifugal Casting Al-Cu Alloy

Effects of Solution Treatment on Microstructure Evolution and Mechanical Properties of Ti-22Al-24Nb-0.5Mo Alloy

Effects of Solution Treatment on Microstructure and Mechanical Properties of Differential Pressure Casting GW103K Alloy

Effect of Solution Treatment on Microstructure and Mechanical Properties of Cast Al–3Li–1.5Cu–0.2Zr Alloy

Microstructure Evolution of Modified Die-Cast AlSi10MnMg Alloy During Solution Treatment and Its Effect on Mechanical Properties

Effect of solution treatment on microstructure and mechanical properties of Cr18Ni10Cu3NbN austenite stainless steel

Effect of Solution Treatment on the Microstructure and Performance of S31254 Super Austenitic Stainless Steel

Effects of Cyclic Heat Treatment on Microstructures and Mechanical ProPerties of Investment Casting TiAl-based Alloy

Effect of Multistage Solid Solution Treatment on Microstructure and Properties of Al-6.5Si-5.5Cu-0.2Zr-0.01Sr-0.06Ti-0.2Y Alloy

Effect of Solution Treatment on Microstructures and Hardness of Mg-Gd-Y-Zr Alloy

Effect of Solution Heat Treatment on the Microstructure and Mechanical Properties of B319 Alloy in the Lost Foam Casting Process

Microstructure and Mechanical Properties of Cast Al-Si-Cu-Mg-Ni-Cr Alloys: Effects of Time and Temperature on Two-Stage Solution Treatment and Ageing

Effects of Solution Treatment on the Microstructure and Mechanical Properties of ZC61 Magnesium Alloy

Effect of solution heat treatment on the internal architecture and compressive strength of an AlMg4.7Si8 alloy

Effects of Solution Treatments on the Microstructure and Mechanical Properties of Inconel 625 Fabricated by Electron Beam Freeform Fabrication

Effect of multi-stage solution on microstructure and properties of Al–10.5Zn–2.05Mg–1.02Cu–0.2Zr–0.923Ti alloy extrusion

Effect of heat treatments on microstructure and mechanical properties of sand cast Al–2Li–2Cu–0.5Mg–0.2Sc–0.2Zr alloy