Autogenous Shrinkage Model for Concrete Accounting for Compounding Effects of Mineral Admixtures

Huan-Chi Ma,Yue Geng,Giovanni Di Luzio,Guo-Dong Li,Yu-Yin Wang
DOI: https://doi.org/10.1016/j.jobe.2024.111503
IF: 7.144
2024-01-01
Journal of Building Engineering
Abstract:The inclusion of mineral admixtures, such as ground granulated Blast Furnace Slag (BFS), silica fume, and fly ash, is gaining popularity in both normal and high-strength concrete in current structural applications to enhance concrete performance at both fresh and hardened states. The double- or triple-adding of mineral admixtures leads to a significant impact on the mixture’s time-dependent behavior, in particular on the autogenous shrinkage. However, a generally applicable prediction model is still not available either in the literature or in the standard codes. This is particularly important for high-strength sealed concrete as the autogenous shrinkage significantly influences the long-term responses, for example, in concrete-filled steel tubular (CFST) columns. To address this issue, a new autogenous shrinkage database concerning the mineral admixture influence on the autogenous shrinkage of sealed cementitious composites, including concrete, mortar, and cement paste, was first set up, which includes a total of 739 shrinkage tests. Next, a new autogenous shrinkage model was then proposed, considering the mineral admixture influence by using the equivalent water-to-binder ratio. This research showed that: (1) the mineral admixture influence on autogenous shrinkage would be more significant for mixes with a lower water-to-binder ratio. This applies to the silica fume, fly ash, and BFS with a specific surface area larger than 400 m2/kg; (2) the BFS or fly ash influence on autogenous shrinkage would be less for mixes with larger silica fume replacement ratio; (3) the opposing effect of BFSs with coarse and fine particles is more pronounced in concrete that has lower water-to-binder ratios. The proposed model offers accurate predictions regarding the autogenous shrinkage of concrete, incorporating all aforementioned features.
What problem does this paper attempt to address?