Abstract:Shotcrete shrinkage and cracking are getting more threatening due to its high content of cementitious materials, small aggregate particle size and a large amount of accelerator, which poses a great threat to the construction safety of engineering structures. This paper studies the volume stability of cement mortar with different contents of fly ash (FA) and granulated blast furnace slag (GBFS) (10%/20%/30%) under the condition that the dosage of alkali liquid accelerator is 4% and that of the alkali-free liquid accelerator is 7%. This work is designed to provide a guidance for the basic research and practical application. By comparing the autogenous shrinkage, drying shrinkage, mass loss caused by drying condition, and internal humidity change of drying condition of cement mortar within 180 days of age. Combined with MIP analysis, XRD hydration product analysis, and SEM hydration product morphology analysis, the results show that both fly ash and granulated blast furnace slag can reduce the autogenous shrinkage and drying shrinkage of cement mortar mixed with accelerator to a certain extent, and the shrinkage reduction effect of FA is more prominent. The reduction effect of GBFS is more obvious at high dosages. Adding FA and high content of GBFS can increase the mass loss of cement mortar under drying shrinkage conditions. The high content of mineral admixtures will exacerbate the rate of decrease in the internal humidity of the cement mortar. The reasons for the reduction of autogenous shrinkage and drying shrinkage of cement mortar mixed with accelerators due to the addition of FA and GBFS are: the early activity of the two mineral admixtures is low, and the hydration process is slow. And the reduction of pore size with the range of 5-50nm leads to the reduction of capillary tensile stress and the weakening of the driving force for shrinkage deformation. Among them, the shrinkage reduction effect of fly ash is more pronounced. Therefore, mineral admixture can be used to replace a certain amount of cement in actual shotcrete construction, so as to increase the volume stability of shotcrete.

Effect of Supplementary Materials on the Autogenous Shrinkage of Cement Paste

Influence of Mineral Admixtures on early Shrinkage of Ordinary Concrete

Unveil the Role of Nano-Caco3 in Early Shrinkage and Tensile Properties of Cement Paste: from Experimental Work to Modeling

Influence of Superplasticizer Type and Dosage on Early-age Drying Shrinkage of Cement Paste with Consideration of Pore Size Distribution and Water Loss

Influence of Superplasticizers on Early Age Drying Shrinkage of Cement Paste with the Same Consistency

Numerical study of the autogenous shrinkage of cement pastes with supplementary cementitious materials based on solidification theory

The Early-Age Drying Shrinkage of Cement-Based Materials with the Same Workability after Temperature Compensation

Experimental and numerical study on the mitigation of autogenous shrinkage of cementitious material

THE AUTOGENOUS SHRINKAGE OF CONCRETES PREPARED WITH THE BINDERS CONTAINING DIFFERENT KINDS OF MINERAL ADMIXTURE

Influence of Recycled Cement Paste Powder on Early-Age Plastic Shrinkage and Cracking of Cement-Based Materials

Effect of Supplementary Cementitious Materials on the Resistance of Cement Paste to Carbonic Acid Water

Effects of Retarding Admixture, Superplasticizer and Supplementary Cementitious Material on the Rheology and Mechanical Properties of High Strength Calcium Sulfoaluminate Cement Paste

The Influence and Application of Slag, Fly Ash, and Limestone Flour on Compressive Strength of Concrete Based on the Concrete Compressive Strength Development over Time (CCSDOT) Model

Unified shrinkage model for concrete from autogenous shrinkage test on paste with and without ground-granulated blast-furnace slag

Shrinkage of blended cement concrete with fly ash or limestone calcined clay

Effect of High Calcium Fly Ash, Ladle Furnace Slag, and Limestone Filler on Packing Density, Consistency, and Strength of Cement Pastes

Autogenous shrinkage of shrinkage-compensating concrete

Effects and Evaluation on Cracking of Concrete Incorporating Supplementary Cementitious Materials(SCM)

Influence of fly ash and granulated blast furnace slag on autogenous shrinkage and drying shrinkage of cement-based materials mixed with alkali accelerator and alkali-free accelerator

Investigating the effects of seawater and sea sand aggregates and supplementary cementitious materials on the early shrinkage and crack resistance of concrete

Effects of SCMs Particles on the Compressive Strength of Micro-Structurally Designed Cement Paste: Inherent Characteristic Effect, Particle Size Refinement Effect, and Hydration Effect