Corrosion Performance and Microstructure Characterization of AA4343/AA3003/AA4343 Laminated Sheets Via Cryorolling and Subsequent Annealing

GOLAM SAMDANE,WAQAS FARID,AHMED FOULY,CHARLIE KONG,YU HAILIANG

DOI: https://doi.org/10.1016/j.mtcomm.2024.111085

IF: 3.8

2024-01-01

Materials Today Communications

Abstract:This study investigates the microstructural evolution, corrosion behavior, and electrochemical properties of AA4343/AA3003/AA4343 laminated sheets subjected to cryorolling (CR) and room-temperature rolling (RTR) under various annealing conditions. The results consistently show that CR samples exhibit superior corrosion resistance compared to RTR samples. While CR sheets primarily experience pitting and uniform corrosion, RTR sheets show more pronounced cracking and deeper pitting, particularly after annealing. Electrochemical analysis indicates that CR samples maintain a more stable corrosion pattern, with the AA4343 clad layer demonstrating improved anodic stability and corrosion resistance during annealing. In contrast, the corrosion potential of the RTR clad layer significantly decreases with extended annealing, indicating a higher susceptibility to corrosion. SEM and EDS analyses reveal that CR samples undergo localized pitting and uniform corrosion, whereas RTR samples experience more severe pitting and crack corrosion, which is further aggravated by irregular elemental distribution. The behavior of second-phase particles, such as α-Al(Fe, Mn)Si phase, plays a crucial role in influencing corrosion. Annealing facilitates uniform distribution and coarsening of these second-phase particles, which helps reduce the number of active corrosion sites.