Abstract:Magnesium (Mg) alloys are promising candidates for use as biomedical implant materials. However, their very fast degradation rate greatly restricts their application. A rare earth phase possessed with a long‐period stacking‐ordered (LPSO) structure was in favor of enhancing the degradation resistance of Mg alloys. In fact, the formation of the LPSO phase in Mg alloys depends on their stacking fault energy. The lower the stacking fault energy, the more the LPSO phase formed. In this study, manganese (Mn) was alloyed to Mg alloy ZK30–10Gd (containing 3 wt.% Zn and 10 wt.% Gd) via selective laser melting to promote the formation of the LPSO phase. As an alloying element, Mn could be in favor of reducing stacking fault energy due to the fact that the large difference between the atomic radius of Mn and that of Mg induced large lattice distortion to facilitate forming stacking faults. The results showed that as the Mn content increased from 0 to 1.2 wt.%, the area fraction of LPSO phase increased from 12.22% to 22.37%, meanwhile the area fraction of (Mg,Zn)3Gd phase decreased from 9.31% to 2.32%. The ZK30–10Gd–0.6Mn possessed the highest degradation resistance (weight loss rate 0.38 mg · cm−2 · day−1). The enhancement of degradation resistance had two reasons. On the one hand, more LPSO phase provided more sites for nucleation of degradation products, which could promote the formation of a homogeneous and compact degradation product film to protect the Mg matrix. On the other hand, the inhibition of (Mg,Zn)3Gd phase precipitation could reduce galvanic corrosion.

Insights into Corrosion Behavior of Mg Alloys Containing Long-Period Stacking Ordered Structure in Chloride and Sulfate Media

Microstructure characterization and corrosion behavior of Mg–Y–Zn alloys with different long period stacking ordered structures

Effect of the Morphology of Long-Period Stacking Ordered Phase on Mechanical Properties and Corrosion Behavior of Cast Mg-Zn-Y-Ti Alloy

Role of the LPSO Structure in the Improvement of Corrosion Resistance of Mg-Gd-Zn-Zr Alloys

Effect of long period stacking ordered structure on the biocorrosion resistance and osteogenesis ability of Mg–Zn–Y-Mn alloys

Effect of Volume Fraction of LPSO Phases on Corrosion and Mechanical Properties of Mg-Zn-Y Alloys

Microstructure and Corrosion of Cast Magnesium Alloy ZK60 in NaCl Solution

Optimization of the Experimental Parameters Affecting the Corrosion Behavior for Mg–Y–Zn–Mn Alloy via Response Surface Methodology

Mn‐promoting formation of a long‐period stacking‐ordered phase in laser‐melted Mg alloys to enhance degradation resistance

Comparative Study on Corrosion Behavior and Mechanism of As-Cast Mg–Zn–Y and Mg–Zn–Gd Alloys

Corrosion Behavior of Mg-Zn-Y-Zr Alloys in Nacl Solution

Interfacial Dislocations Dominated Lateral Growth of Long-Period Stacking Ordered Phase in Mg Alloys

Engineering Atomic-to-Nano Scale Structural Homogeneity towards High Corrosion Resistance of Amorphous Magnesium-Based Alloys

Elucidating the dependence of corrosion behavior and mechanical property on the grain structure of low-temperature as-extruded Mg–Zn–Ca–Zr alloy

In-situ AFM and quasi-in-situ studies for localized corrosion in Mg-9Al-1Fe-(Gd) alloys under 3.5 wt.% NaCl environment

Corrosion behavior of magnesium and its alloy in NaCl solution

Study of the corrosion mechanism of Mg–Gd based soluble magnesium alloys with different initial texture states

Microstructure and corrosion behavior of as-homogenized and as-extruded Mg−xLi−3Al−2Zn−0.5Y alloys (x=4, 8, 12)

Microgalvanic Corrosion of Mg–Ca and Mg–Al–Ca Alloys in NaCl and Na2SO4 Solutions

Influence of β-Mg 17 Al 12 and Al-Mn intermetallic compounds on the corrosion behaviour of cast and solution treated Mg-Al-Zn-Mn alloys

Effect of volume fraction of 18R-LPSO phase on corrosion resistance of Mg−Zn−Y alloys