Excellent Tensile Strengthening and Corrosion Resistance of M50 Bearing Steels by Plasma Torch Surface Nitrogen Atoms Injection

Hainan Zhang,Jianbo Yu,Zhigang Yang,Jintao Jiang,Ying Dong,Xiaoxin Zhang,Jiang Wang,Zhongming Ren

DOI: https://doi.org/10.1016/j.mtcomm.2024.111077

IF: 3.8

2024-01-01

Materials Today Communications

Abstract:The application of M50 bearing steels in the harsh environments of aerospace bearings demands extremely high strength and corrosion resistance. Utilizing new technologies for surface strengthening of M50 bearing steels are key to enhancing its service life and safety. Therefore, in this paper, tensile strength and corrosion resistance of M50 bearing steels prepared by novel plasma torch surface nitriding technology were investigated. Results showed that compared to the original M50 bearing steels, the number of large, irregular harmful carbides were significantly reduced in the as-nitrided M50 bearing steels, transforming into fine, dispersed nitrogen-containing precipitates. The nitrogen content increased up to 0.42%, resulting in a maximum reduction in precipitate size and area by 93% and 92%, respectively. The tensile strength of the nitrided M50 bearing steel was improved by up to 50%, compared to the original M50 steels of 706MPa, which was mainly attributed to the synergistic effects of lattice distortion caused by nitrogen atoms in the matrix, the obstruction of dislocations by nitrogen-containing precipitates, and the martensitic structure. Meanwhile, the corrosion current density of the nitrided samples was reduced by up to 62%. The reason was that the chromium depletion phenomenon disappeared owing to that the nitrogen and alloying elements were uniformly distributed in the matrix. The novel plasma nitriding technology has shown significant effects in enhancing the surface strength and corrosion resistance of M50 bearing steels.