Abstract:M50 steel is a commonly used material for aeroengine main shaft bearings. In this study, a gradient nanostructured M50 steel was fabricated by an efficient surface nanocrystallization method, i.e., ultrasonic shot peening (USP) technology. The recrystallization behavior and phase transformation of gradient nanostructured M50 steel under the athermal effect of electrical pulses were investigated. Compared with the USPed sample, the ferrite structure size was 32.5% smaller, and the structure size uniformity was 51.5% greater in the 0–50 μm region after USP treatment and electrical pulsing treatment (EPT) with 38 A/mm 2 –1 s. Athermally induced ferrite recrystallization by EPT accompanied with obvious precipitation of VC and Mo 2 C carbides, and decomposition of austenite occurred during ferrite structure coarsening. EPT has different responses to different depths of gradient M50 steel, and there is an optimal current density to achieve structure refinement in different depths. However, the coarse-grain tempered M50 steel did not undergo obvious ferrite structure refinement under the same EPT parameters. The results revealed that the EPT promoted static recrystallization of incompletely recrystallized structures after USP processing by activating the release of stored deformation energy. Static recrystallization under the athermal effect of EPT was achieved by promoting the migration of the subgrain boundary to absorb the surrounding dislocations and increase the misorientation between itself and the surrounding ferrite structure. The mechanism of the athermal effect of EPT was based on electron-defect interactions, such as dislocations and lattice distortions. High-density nonequilibrium grain boundaries, acting as "active sites", accelerating the process of recrystallization under the effect of electric pulses. This study proposed a method for optimizing EPT parameters through the change in instantaneous resistance to evaluate the degree of recrystallization of the gradient structure.

Graded Microstructure and Mechanical Performance of Ti/N-Implanted M50 Steel with Polyenergy.

Graded Microstructure and Mechanical Performance of Ti/N-Implanted M50 Steel with Polyenergy

A Study of the Corrosion Resistance of M50NiL Bearing Steel by Ion Implantation

The microstructure and tribological properties of M50 steel surface after titanium ion implantation

Microstructure and Mechanical Properties of Ti + N Ion Implanted Cronidur30 Steel.

Mechanism of Mechanical Property Enhancement in Nitrogen and Titanium Implanted 321 Stainless Steel

Understanding the thermal stability and friction behavior of ultrasonic shot peening-introduced gradient nanostructured M50 bearing steel

Understanding the recrystallization and phase transformation of gradient nanostructured M50 steel under the athermal effect of electrical pulses

Microstructure and Mechanical Properties of Ti60-Ti2alnb Functionally Graded Materials Fabricated by Laser Directed Energy Deposition

Enhanced Wear Resistance of the Ultrastrong Ultrasonic Shot-Peened M50 Bearing Steel with Gradient Nanograins

Study of surface modification of metal ion-implanted with TiN

Microstructure and mechanical properties of surface layer of M50NiL steel plasma nitrided

The Cavitation Erosion of the Mild Carbon Steels Implanted with Titanium and Nitrogen

Microstructure Formation and Mechanical Properties of Metastable Titanium-Based Gradient Coating Fabricated via Intense Pulse Ion Beam Melt Mixing

The Cavitation Erosion of the 45# Carbon Steels Implanted with Titanium and Nitrogen

Microstructure and mechanical properties of TC4/NiTi bionic gradient heterogeneous alloy prepared by multi-wire arc additive manufacturing

Athermally induced MC carbide decomposition in gradient M50 bearing steels during electric pulse treatments

Nitriding behavior and mechanical properties of carburizing and nitriding duplex treated M50NiL steel

Structure and mechanical properties of graded Cr/CrN/CrTiN coatings synthesized by close field unbalanced magnetron sputtering