The Cavitation Erosion of the Mild Carbon Steels Implanted with Titanium and Nitrogen

Liu Fengbin,Chen Darong,Zhao Ming,Wang Jiadao,Xu Yanji

DOI: https://doi.org/10.1007/978-3-642-03653-8_258

2009-01-01

Abstract: The polished 0.45% C steels (45# steels) were implanted with titanium, nitrogen and titanium+nitrogen at fluence of 2×1017 ions/cm2, 2×1017 ions/cm2 and 4×1017 ions/cm2, respectively. To evaluate the cavitation erosion resistances of the ion-implanted 45# steel samples, the cavitation erosion experiments were carried out by using rotating disk facility. The surface hardness and the polarization potentials corresponding to the ion-implanted samples were also investigated by using nano-indentation tester and electrochemical techniques. The results showed that relative to the initial 45# steel, the surface nanohardness and the polarization potentials corresponding to the ion-implanted 45# steel samples all improve to varying degrees. The cavitation erosion resistances corresponding to these ion-implanted samples enhance with the increase of their polarization potentials. However, it seemed that it is little affected by the surface hardness. To elucidate the cavitation erosion resistance of the ion-implantde 45# steel samples, the phase structures of the steel samples implanted with Ti, N and Ti/N were studied by using X-ray diffraction (XRD). The results indicated that the ion-implantation alters the structure of the 45# steel and new phases form. The new phases are the domination factors that have contributions to the improvements of the surface properties of the samples.