Outstanding Strength-Ductility Combination in NAB Alloy Via Coarse Widmanstätten Α Phases and Ultrafine (α+κ) Lamella Structure

Xiaobin Yang,Deyun Liu,Siyu Kuang,Kai Yin,Cong Ye,Yiheng Dong,Jiang Ju,Zhao Shen,Shuo Ma,Liming Fu,Aidang Shan
DOI: https://doi.org/10.1016/j.msea.2024.147565
IF: 6.044
2024-01-01
Materials Science and Engineering A
Abstract:By optimizing the partitioning of alloying elements through the metastable Widmanstätten transition, an exceptional combination of strength and ductility in hot-forged nickel aluminum bronze (NAB) alloys was achieved using a modified quenching-aging-tempering (Q-A-T) stepwise heat treatment process via incorporating an air-cooling step before quenching for Widmanstätten transition. The composite structure by this process, comprising mainly coarse Widmanstätten α grains and ultrafine (α+κ) lamella structures, yielded a tensile strength of approximately 1000 MPa and elongation of 11-28%. Compared with the traditional method of reducing the solution temperature to the dual-phase temperature, introducing the α phases in equilibrium, the strategic utilization of the Widmanstätten transition reduces the excessive precipitation of the micro-sized κ phase before quenching. It enhances the precipitation of the nano-sized κ phase during aging, which significantly refines the martensite decomposition products, particularly the (α+κ) lamella structure, through a pinning effect, significantly improving the strength of the alloy. Additionally, alloying elements supersaturated in the Widmanstätten structure precipitate as nano-sized κ phases during subsequent aging and tempering, thereby improving the strength and work-hardening ability of the coarse Widmanstätten structure, which is a beneficial characteristic not typically associated with the α phase in equilibrium.
What problem does this paper attempt to address?