Abstract:Stress Corrosion Cracking (SCC) is a failure mechanism that occurs when certain materials are subjected to both external or residual stresses and corrosion. This combined effect leads to the development of cracks in the susceptible materials. Submerged steel pipelines in the petroleum sector are built of low-alloy steels having a ferrite-cementite composition, including API 5L X70. Such materials are sensitive to SCC damage in aqueous systems. The film rupture dissolution repassivation (FRDR) process is used in this study to evaluate the cracks and pits growth in oil and gas pipelines in the Gulf area under diverse SCC environmental conditions. The SCC crack propagation and pit growth under near-neutral environmental conditions were analyzed using phase field modelling. X70 steel under NS4 the solution was used for the analysis to represent the anodic dissolution film rupture mechanism. A parametric study was done to study the impact of different electrochemistry and phase field parameters on crack growth behaviour. The study assess the susceptibility to SCC caused by an pit by employing diverse settings to evaluate the impact of corrosion parameters and the interaction among the FRDR mechanism. The corrosion rates are influenced by the interface kinetics coefficient (L), which exhibits an accelerated effect as L increases. This transition from fracture-controlled to dissolution-controlled SCC growth occurs until the system reaches the diffusion limit, beyond which further increases in L do not significantly impact corrosion rates. Moreover, higher values of the kinetic coefficient (k) advance the creation of SCC cracks at the crack front, resulting from corrosion originating from pitting at the crack mouth. This process leads to the refinement of the pit and its transformation into a crack. A comparison analysis was utilized to validate our simulation under a near-neutral NS4 solution for X70 steel by correlating the findings with other numerical methods for crack growth utilizing the same material and environmental parameters. The results show decent agreement with the comparative study.

Analysis of Stress Corrosion Cracking Failure of 316L Stainless Steel Flow Promoter String in the Aggressive Oilfield Environment

Corrosion crack failure analysis of 316L hydraulic control pipeline in high temperature aerobic steam environment of heavy oil thermal recovery well

Analysis of Stress Corrosion Cracking Growth Rate in the Heat-Affected Zone of 316L Based on the Heterogeneity of the Mechanical Properties

Observations of Stress Corrosion Cracking in Pipeline Steel in Corrosive Seawater Environment Including Detailed Observation of the Crack Initiation Mechanism

Analysis of the causes of the cracking of tube bundles of 316L stainless steel Shell-and-Tube heat exchanger

An Investigation of Corrosion-Induced Stress During SCC

Stress corrosion cracking under extreme near-neutral GCC conditions, parametric and comparative study using phase field modeling

Correlating oxidation resistance to stress corrosion cracking of 309L and 308L stainless steel claddings in simulated PWR primary water

On the corrosion cracking of austenitic stainless steel in molten solar salt: Experiments and modeling

Stress Corrosion Cracking of 2205 Duplex Stainless Steel with Simulated Welding Microstructures in Simulated Sea Environment at Different Depths

A Three-Dimensional Model of Non-Slipping Stress Corrosion Cracking under Low Loads

Stress corrosion cracking behavior of super 13Cr tubing in phosphate packer fluid of high pressure high temperature gas well

Fracture Mechanics Analysis Of The Stress Corrosion Cracking Failure Of Stainless Steel Hexagonal Head Screws In A Marine-Industrial Environment

Investigation of the Effect of pH on Stress Corrosion Cracking of API 5L X65 Steel by Impedance Spectroscopy and Slow Strain Rate Tensile Test

Study on Corrosion Fatigue Behavior of 304L Austenite Stainless Steel in 325 °C High-Temperature Water Environment

STRESS CORROSION CRACKING BEHAVIOR OF A NEW KIND OF ULTRAHIGH STRENGTH STEEL Cr12Ni4Mo2Co14 IN ACID ENVIRONMENT

Investigation of Multi-Factor Stress Corrosion Cracking Failure of Safe-End Feedwater Lines of Submarine Power System

Characteristic of Acoustic Emission Signal from Stress Corrosion Cracking in Low-Carbon Nitrogen-Enhanced Stainless Steel

Fractography of Stress Corrosion Cracking of 20% Cold Worked Type 304 H Stainless Steel Containing δ-Ferrite in Oxidizing Primary Water

Corrosion Behavior of Tubing in High-Salinity Formation Water Environment Containing H2S/CO2 in Yingzhong Block

Microstructurally and mechanically small fatigue crack growth behaviors of 316LN stainless steel in high-temperature pressurized water