Ultra-high Temperature Ceramic TaC Precursor with High Ceramic Yield and Low Oxygen Content after Pyrolysis Enhanced by Carbon Source Chelated Three-Dimensional Network Structure

Xinyuan Zhang,Fuping Li,Kang Zhao,Zhao Zhang,Hua Jiao,Qingnan Meng,Yufei Tang

DOI: https://doi.org/10.1016/j.ceramint.2024.11.231

IF: 5.532

2024-01-01

Ceramics International

Abstract:Development of UHTCs precursors with a high ceramic yield, low viscosity at high solid content, and low oxygen content of after pyrolysis is crucial for UHTCs-modified C/Cs composites fabricated by PIP process. In the present work, four types of TaC precursors with varying microstructures were designed and synthesized. The effects of the precursor microstructure on the morphology, size, ceramic yield and oxygen content after pyrolysis were investigated. The findings demonstrate that the three-dimensional network structure may lower the oxygen content of pyrolysis products and that the carbon source chelated structure can significantly increase the ceramic yield of TaC precursor. After pyrolysis at 1500°C, the ceramic yield of the TaC precursor, TCP-4, was 51.80 wt.%, and the oxygen content of the pyrolysis product was only 0.48 wt.%. The TCP-4 ethanol solution at 90 wt.% viscosity is 67.03 mPa·S which meets the requirements of the PIP process. The formation thermodynamics of carbon source chelated three-dimensional network structure is analyzed. The present work not only provides a high-performance TaC precursor, but also offers a novel idea and approach for development of other ultra-high temperature ceramic precursors.