Abstract:Using molecular dynamics simulation, we studied the dynamic behavior and microscopic mechanisms of near-surface helium bubble in single crystal Cu subjected to shock loading. The whole process of bubble evolution includes three stages: shock compression, equilibration, and expansion-rupture-ejection. When shock wave reaches the bubble, it is compressed and an internal jetting is formed, leading to the increases of velocity and internal pressure of the bubble. The internal pressure then reduces slightly due to the relaxation of helium atoms. After the reflected rarefaction wave reaching the bubble, the internal pressure greatly decreases to several GPa and the volume expands a lot. Because of the pressure gradient between the bubble and the free surface, the velocity of the bubble increases again, squeezing the upper thin metal layer continuously and finally making it plastically fail or melt. Then the bubble ruptures, ejecting helium atoms and some Cu clusters. Impact strength has significant effects on this dynamic process. Higher impact velocity leads to stronger jet and more significant expansion and rupture of the bubble. The latter is attributed to the microstructure evolution of the surrounding metal atoms and the upper metal layer, for which plastic failure or melt is observed at higher impact velocity. The influences of helium bubble size and number ratio of He/vacancy are also investigated. We find that the internal jet is stronger and temperature rise and local melting of metal is more obvious for larger bubble, resulting in easier failure of the metal layer and thus more remarkable expansion and rupture of the bubble. Higher number ratio results in weaker internal jet but stronger expansion and rupture of the bubble. This is because more helium atoms in the bubble for higher ratio can impact on the upper metal layer, leading to easier failure of the metal layer.

The dynamic response of He bubble in bicrystal copper under uniaxial compression and tension

The growth and coalescence of helium bubbles in bicrystal copper under tension

Mechanism of nanoscale helium bubbles influencing dynamic tensile response of polycrystalline copper

Shock Response of He Bubbles in Single Crystal Cu

The Shock-Induced Deformation and Spallation Failure of Bicrystal Copper with a Nanoscale Helium Bubble via Molecular Dynamics Simulations

The rupture and ejection of near-surface helium bubble in single crystal Cu under shock loading

Shock response of He bubble in single crystal tungsten: molecular dynamics simulation study

Atomistic simulation and continuum modeling of the dynamic tensile fracture and damage evolution of solid single crystalline Al with He bubble

Molecular Dynamics Study on the Nano-Void Growth and Coalescence at Grain Boundary

Atomistic simulation of brittle-to-ductile transition in silicon carbide embedded with nano-sized helium bubbles

Deformation and Spallation of Shocked Cu Bicrystals with Σ3 Coherent and Symmetric Incoherent Twin Boundaries

Computational Simulation of He Bubble Evolution in Fcc Cu with Σ3 Twin Boundary Using Object Kinetic Monte Carlo Method

Multiaxial Behavior of Nanoporous Single Crystal Copper: a Molecular Dynamics Study

Effect of grain boundaries and rigid inclusions on plasticity in nickel bicrystals containing helium bubbles and radiation-induced self-interstitial atom clusters

Influence of grain boundaries on the loop-punching mechanism and shape of helium bubbles in tungsten

Effects of Local Structure on Helium Bubble Growth in Bulk and at Grain Boundaries of Bcc Iron: A Molecular Dynamics Study

Influences of Symmetric Tilt Grain Boundary on the Stretching Deformation Behaviors of Cu Bicrystals

Shock Response of Copper Bicrystals with a ∑3 Asymmetric Tilt Grain Boundary

Left-Right Loading Dependence of Shock Response of (111)//(112) Cu Bicrystals: Deformation and Spallation

Shock Wave Loading And Spallation Of Copper Bicrystals With Asymmetric Sigma 3 < 110 > Tilt Grain Boundaries

Modeling irradiation-induced intragranular gas bubble in tungsten under external tensile loading