Abstract:Defects introduced during additive manufacturing currently control fatigue resistance and lead to a large scatter in lifetime, with pancake shaped lack of fusion (LOF) defects being particularly potent. In this study the fatigue crack propagation life of selective laser-melted (SLM) AlSi10Mg alloy is considered in cases where single cracks and multiple cracks can initiate from LOF defects under high cycle fatigue (HCF). Firstly, the aspect ratios of initially long fatigue cracks were determined for critical LOF defects obtained from X-ray CT renderings using the critical defect regularization method, and the response surface method used to obtain the stress intensity factor of the crack front quickly and continuously. Then a single crack propagation model considering the evolution of the crack aspect ratio established to predict the crack propagation life which is in good agreement within in situ X-ray CT imaging of the crack front when a single crack is dominant. The crack propagation phase was predicted to represent 35–60% of the total fatigue life representing a larger fraction at high stress amplitudes. Multiple cracks were found to initiate cracks at the larger stress amplitudes. In cases where multiple cracks arise this is non-conservative and so a synergistic multiple fatigue crack growth (smFCG) model was developed based on multiple defects measured a priori by X-ray CT to depict the competitive cracking effect. Compared with the single crack model, the smFCG model predicts a shorter propagation life (by 5–10%) when multiple defects are involved since it considers all the initial defects within the crack initiation region. Given the propensity of large numbers of defects in AM material this approach may be more appropriate in many cases.

In-situ SEM investigation and modeling of small crack growth behavior of additively manufactured titanium alloy

Modelling the Variability and the Anisotropic Behaviour of Crack Growth in SLM Ti-6Al-4V

In-situ investigation on the anisotropic behavior of the additively manufactured dual-phase Ti-6Al-4V alloy

Study on Fatigue Crack Growth of Electron Beam Selective Melting of Titanium Alloy

In situ X-ray imaging of fatigue crack growth from multiple defects in additively manufactured AlSi10Mg alloy

Characteristic and mechanism of crack initiation and early growth of an additively manufactured Ti-6Al-4V in very high cycle fatigue regime

Fatigue Crack Growth Rates and Crack Tip Opening Loads in CT Specimens Made of SDSS and Manufactured Using WAAM

Discovering the role of the defect morphology and microstructure on the deformation behavior of additive manufactured Ti–6Al–4V

Effect of microstructure on short fatigue crack growth of wire arc additive manufactured Ti-6Al-4V

In-situ SEM Investigation on Fatigue Behaviors of Additive Manufactured Al-Si10-Mg Alloy at Elevated Temperature

Fatigue crack growth behavior in an aluminum alloy Al–Mg–0.3Sc produced by wire based directed energy deposition process

Ductile fracture prediction of additively manufactured Ti-6Al-4 V alloy based on void growth and coalescence of a unit-cell model

Ductile fracture prediction of additive manufactured Ti6Al4V alloy based on an extended GTN damage model

Fatigue Crack Segmentation and Characterization of Additively Manufactured Ti‐6Al‐4V Using X‐Ray Computed Tomography

In-Situ SEM Study on Deformation and Failure Mechanism of TC4 Titanium Alloy by Laser Additive Manufacturing

Composition-induced microcrack defect formation in the twin-wire plasma arc additive manufacturing of binary TiAl alloy: An X-ray computed tomography-based investigation

Crystallographic analysis for fatigue small crack growth behaviors of a nickel-based single crystal by in situ SEM observation

TEM analysis of quasi in-situ formed tensile and fatigue cracks in a dual-phase Ti alloy

Experimental and Modeling Study on Small Fatigue Crack Initiation and Propagation Behavior of Inconel 617

Study on Small Fatigue Crack Growth Rate of SLM AlSi10Mg Alloy

Modeling and Simulation Investigations on Microstructure Evolution during Additive Manufacturing of AlSi10Mg Alloy