Microstructural Evolution and Mechanical Properties of Al-4Ni-0.4 V Alloyed with Zr and Ti at Elevated Temperatures

Xu Chen,Ji Chen,Weiguo Xi,Qizhou Cai,Jingfan Cheng,Wenming Jiang
DOI: https://doi.org/10.1016/j.jallcom.2024.177052
IF: 6.2
2025-01-01
Journal of Alloys and Compounds
Abstract:The influence of Zr and Ti alloying on the microstructural evolution and mechanical properties of an Al-4Ni-0.4V alloy at elevated temperatures was investigated. The results showed that the coarsening rate of the eutectic Al3Ni phase in the Al-4Ni-0.4V-0.2Zr-0.2Ti alloy decreased from 21.1 nm3/s in the Al-4Ni-0.4V alloy to 7.4 nm3/s after annealing at 350 degrees C for 0 h to 120 h. The tensile strength, yield strength, and elongation at room temperature of the annealed Al-4Ni-0.4V-0.2Zr-0.2Ti alloy (350 degrees C, 8 h) were 181 MPa, 108 MPa, and 27.2 %, respectively. After tensile test at 350 degrees C, these values of the annealed Al-4Ni-0.4V-0.2Zr-0.2Ti alloy were 108 MPa, 72 MPa, and 29.8 %, respectively. Transmission electron microscopy results revealed the precipitation of the L12 ordered structure of the Al3M (M = Zr, V, Ti) phase, approximately 2 nm in size, in the alpha-Al after annealing. These phases exhibited excellent lattice matching with the alpha-Al and considerable precipitation strengthening. Segregation of Zr, V, and Ti elements at the alpha-Al/Al3Ni interface hindered Ni diffusion in the matrix, thereby reducing Al3Ni phase coarsening. Moreover, the Al3M phase precipitated at the interface exhibited favorable matching with the lattice planes of the alpha-Al and Al3Ni phase, which improved the thermal stability of the eutectic structure and the mechanical properties at elevated temperatures.
What problem does this paper attempt to address?