Fabrication of MgB2 Coil with the Center Field of 5.71 Tesla Using 520‐m Inner Magnesium Diffusion Wire
Zhenyu Chen,Fang Yang,Qingyang Wang,Jianqing Feng,Jixing Liu,Rui Zhang,Dayou Wang,Shengnan Zhang,Jianfeng Li,Pingxiang Zhang
DOI: https://doi.org/10.1002/adfm.202413300
IF: 19
2024-11-18
Advanced Functional Materials
Abstract:IMD MgB2 long wire is produced by alternating use of rotary‐swaging and drawing strategy. A 600 m 30‐filament MgB2 wire is obtained here with the Je and Jc reaches to 8.0 × 104 A cm−2 and 7.6 × 105 A cm−2 (at 4.2 K, 4 T), respectively. The MgB2 coil made by the wire obtains a center field of 5.71 T. The poor deformation ability of magnesium rods makes it challenging to fabricate long MgB2 inner magnesium diffusion (IMD) wires, further seriously limiting the application of high‐performance MgB2 wires. A 600 m IMD 30‐filament MgB2 wire is fabricate by alternating use of rotary‐swaging and drawing strategy. The critical current density (Jc) and the critical engineering current density (Je) are 8.0 × 104 A cm−2 and 7.6 × 105 A cm−2 (at 4.2 K, 4 T), respectively, which are some of the best performances reported so far. The flux‐pinning behavior of the MgB2 wires is investigated, and the surface pinning behavior is found to be dominant in the IMD 30‐filament wire in the whole field range at 4.2 K. The critical point for the IMD 30‐filament MgB2 wire to keep high performance in high fields is revealed by comparing it with the reference wires. Then, 520 m of wire are cut from the 30‐filament MgB2 wire and wound into a coil. The center field of the coil is 5.71 T at 4.2 K when the current loads to 219 A, which is the highest value among the IMD MgB2 coils. This work made breakthroughs in the wire length, filament numbers, and transport performance of IMD MgB2 wire, while also providing a paradigm study for exploring the in situ magnetic performance of multi‐filament wires.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology