Mechanical and superconducting properties of kilometer level,Nb reinforced,6+1 filamentary MgB_2wires

Wang Qingyang,Yan Guo,Xiong Xiaomei,Yang Fang,Liu Guoqing,Feng Jianqing,Li Chengshan,Feng Yong,Zhang Pingxiang

2013-01-01

Abstract:Kilometer level 6 + 1 filamentary MgB2wires sheathed with Nb / Cu composite tube was fabricated by in-situ powder-in-tube( PIT) method,non-magnetic Nb was employed as the centre reinforced materials. There was no any annealing in the whole fabrication process due to the excellent ductility of Nb / Cu composite tube. The( Mg,B) / Nb / Cu composite wire was fabricated to the target size of 1. 4 mm in diameter and heat treated at 680℃ for 2 hours in a vacuum furnace. Superconductivity,mechanical properties and homogeneity of critical current were measured respectively. The transport engineering critical current density( J ce) reaches 2. 5 ×104A / cm2at 20K,1T. The results show a good potential to fabricate high performance MgB2wires at ambient pressure for practical application.