FABRICATION AND PROPERTIES OF MULTI-FILAMENTARY MgB2 WIRES WITH Nb REINFORCEMENT

王庆阳,闫果,A Sulpic,刘国庆,焦高峰,熊晓梅,冯勇,张平祥

2011-01-01

Abstract:Various structure MgB2/NbCu multi-filamentary wires with TiC doping was fabricated by the in-situ powder-in-tube(PIT) technique with Nb bar as the centre reinforcement materials.The MgB2/NbCu multi-filamentary wires were heat-treatment at 700℃ for 2 hours on flowing argon.The stress-strain properties,microstructure and superconducting properties of MgB2 wires were analysis,respectively.The stress-strain results show that the Nb reinforcement can enhance the mechanics properties obviously.The microstructure analysis shows the good grain connection and higher density was obtain.The transfer critical current density was measurement by the standard four-probe wires technique at 4.2 K.The result indicates that this technique can fabricated applied multi-filamentary MgB2 superconducting wires.