Synthesis and Properties of MgB2 Superconducting Wires Fabricated by Extrusion Method

Wang Dayou,Shan Di,Yan Guo,Wang Qingyang,Feng Yong,Zhang Pingxiang

DOI: https://doi.org/10.13373/j.cnki.cjrm.XY15111801

2017-01-01

Abstract:MgB2 superconducting wire of kilometers could be prepared by powder in tube method (PIT).But it still could not fully meet the requirements of application.How to improve the length of single wire was still an important research field of MgB2 superconducting material.In the traditional PIT process,the extrusion method was introduced.Two MgB2 composite wires were fabricated with the extrusion procedure,where Cu and Cu-Nb bars were adopted as central strengthening cores,respectively.Two superconducting wires with a diameter of 3 mm were processed by extrusion and drawing.The morphology of the cross section and fracture surface was analyzed by means of optical microscope (OM) and scanning electron microscope (SEM).The Icc-B curve of the sample was measured with 1 μV ·cm-1 voltage criterion and standard four-probe method.The Jc-B curves of the samples at the temperature were calculated.Ic was critic current,B was magnictic field strength,Jc was critic current density.The deformation of all components of the extrusion process was found to be synchronized.The extrusion technology could effectively increase the density of core wire.At 4 T,4.2 K,the Jc of MgB2 with Cu and Cu-Nb core reached 2.48 × 104 A·cm 2 and 1.59 × 104 A·cm-2.It was feasible to process the MgB2 superconducting wires by extrusion technology,but the current use of the conductor structure needed to be further optimized.