Enhancing Piezoelectric Properties of BiScO3-PbTiO3 Ceramics Via- Incorporation of Bi(Zn1/2Ti1/2)O3 with High Spontaneous Polarization

Mingwen Wang,Fenghua Tian,Chunchun Li,Shuai Yang,Jie Wu,Jinglei Li,Xuechen Liu,Jinjing Zhang,Fei Li

DOI: https://doi.org/10.1016/j.jeurceramsoc.2024.116945

IF: 5.7

2025-01-01

Journal of the European Ceramic Society

Abstract:High-performance piezoelectric materials are the core elements for the fabrication piezoelectric transducers and actuators. In recent years, there has been an increasing demand for piezoelectric materials with both high operational temperature and large piezoelectricity. However, the conventional approach of soft doping to enhance the piezoelectric response often results in a reduction in Curie temperature. To address this issue, we incorporated Bi(Zn1/2Ti1/2)O-3 with a large spontaneous polarization (P-s similar to 100 mu C/cm(2)) and high Curie temperature (T-c similar to 1380 degrees C) into BiScO3-PbTiO3 ceramics to improve the piezoelectric response while maintaining high T-c. The newly developed 0.08Bi(Zn1/2Ti1/2)O-3-0.335BiScO(3)-0.585PbTiO(3) ceramic exhibits impressive properties including a high d(33) value of 585 pC/N (increased by similar to 33 % compared to the 0.36BiScO(3)-0.64PbTiO(3) ceramics), an electromechanical coupling coefficient k(33) of 0.75, a dielectric constant epsilon ' of 2380, a relatively high T-c of 421 degrees C. These remarkable improvements hold great promise for advancing high-temperature piezoelectric devices.