Realizing excellent electromechanical coupling performance in BiScO3-Bi(Zn2/3Nb1/3)O3-PbTiO3 ternary high-temperature perovskite ceramics

Xiaole Yu,Shihua Jiang,Kaibiao Xi,Wenlong Xu,Mupeng Zheng,Mankang Zhu,Yudong Hou

DOI: https://doi.org/10.1016/j.jeurceramsoc.2024.02.054

IF: 5.7

2024-02-01

Journal of the European Ceramic Society

Abstract:Large piezoelectric voltage coefficient (g 33) and figure of merit (FOM 33) are the key parameters of perovskite ceramics for piezoelectric sensors and energy harvesters. Here, the Bi(Zn2/3Nb1/3)O3 (BZN) member with a low tolerance factor is introduced into the BiScO3-PbTiO3 (BS-PT) perovskite high-temperature piezoelectric matrix to decouple the piezoelectric coefficient (d 33) and dielectric constant (ε r) by modulating the morphotropic phase boundary and grain size. For the optimal 0.38BS-0.01BZN-0.61PT ceramic that benefits from the decoupling of d 33 and ε r, its Curie temperature, g 33 and FOM 33 are as high as 436 °C, 38.6 mV·m·N−1 and 16.5×10−12 m2·N−1, respectively. Furthermore, the 0.38BS-0.01BZN-0.61PT ceramic also shows the technical advantages of large g 33 and FOM 33 even at harsh elevated temperatures (≥ 200 °C). Due to its outstanding comprehensive performances above, the 0.38BS-0.01BZN-0.61PT ceramic surpasses many other BS-PT-based piezoceramics. These results demonstrate that the 0.38BS-0.01BZN-0.61PT material is a promising competitor for high-temperature electromechanical coupling applications.

materials science, ceramics