Low-Loss, Temperature-Stable, and Li-Enriched Li2.12ZnTi3O8 Dielectric Ceramics for LTCC Applications with V2O5 Addition

Kui Liu,Huaiwu Zhang,Cheng Liu,Jie Li,Dainan Zhang

DOI: https://doi.org/10.1109/icept63120.2024.10668444

2024-01-01

Abstract:Herein, the sintering characteristics, phase composition, microscopic morphology, Lattice Vibration Characteristics, and dielectric properties in the microwave and terahertz frequency scales of the novel low-temperature cofired ceramics (LTCC) L i2.12 ZnTi 3 O 8 + $x$ V 2 O 5 ( $x$ =0.5-2.0 wt.%) were prepared and investigated. The L i2.12 ZnTi 3 O 8 + 1.5wt.% V 2 O 5 ceramics, sintered at 925 °C for 4 hours, exhibit the optimal microwave dielectric properties: $\varepsilon_{r}=22.42,Q\times f= 49592$ GHz, $\tau_{f}=7.9$ ppm/°C (@8.6 GHz). The generation of VO 2 and liquid phase leads to poorer dielectric properties, while higher densities and larger grain sizes are the main reasons for better microwave dielectric properties. In the terahertz band (0.2 - 1.2 THz), $\varepsilon_{r}$ ranges between 15 and 25 with a dissipation factor as low as 0.001. This suggests that L i2.12 ZnTi 3 O 8 + $x$ V2O 5 ceramics also have a wide range of applications in the terahertz band. L i2.12 ZnTi 3 O 8 + 1.5wt.% V 2 O 5 has exhibited excellent compatibility with silver electrodes. All these results indicate that L i2.12 ZnTi 3 O 8 + 1.5wt.% V 2 O 5 has a promising application in the LTCC field.