Insight into the tribological performance and mechanisms of MoN-Ag/oil solid-liquid lubrication system based on catalytic effect
Yaohong Jiang,Xinmeng Wu,Shunuo Bian,Chunyan Chen,Haiwei Han,Bin Zuo,Kun Lu,Lijun Zhao,Lihua Yu,Junhua Xu
DOI: https://doi.org/10.1016/j.surfcoat.2024.130612
IF: 4.865
2024-03-02
Surface and Coatings Technology
Abstract:Efficiently reducing friction and wear in an environmentally friendly lubrication manner remains a challenging endeavor. Here, carbon-based tribofilms with excellent friction-reducing and anti-wear abilities was in-situ formed from the poly-α-olefin oil (PAO6) on the friction interfaces of MoN-Ag composite films. A series of MoN-Ag films were prepared by multi-target magnetron sputtering process. Then, X-ray diffractometer (XRD), X-ray photoelectron spectrometer (XPS), Transmission electron microscopy (TEM), Scanning electron microscopy (SEM), Raman, and Fourier-transform infrared (FTIR) spectroscopy, etc. were employed to investigate the microstructures, surface morphologies, mechanical properties of the MoN-Ag films, as well as the tribological performance under the luberication of PAO6 oil. The results showed that the MoN-Ag film consists of γ-Mo 2 N and c-Ag. With the increase of Ag content, the surface roughness of the films stays increased, while the hardness and elastic modulus of the films initially increase and then decrease. When the content of Ag is 2.7 at.%, the film had the highest hardness (24.1 GPa) and elastic modulus (316.5 GPa), and the MoN-Ag/oil solid-liquid system exhibited the lowest average friction coefficient of 0.087 and the lowest wear rate of 5.8 × 10 −7 mm 3 N −1 m −1 after a long duration. The catalytic effect of Ag facilitated the degradation of PAO6 molecules on the friction interface, resulting in the in-situ reorganization and formation of amorphous carbon-based tribofilms with graphite-like structures.
physics, applied,materials science, coatings & films