Chemiresistive Flexible Gas Sensor for NO2 Sensing at Room-Temperature Using in Situ Constructed Au@In2S3/In2O3 Hybrid Microflowers

Bingliang Wang,Yongjiao Sun,Yimeng Dong,Yuchen Hou,Zhiyuan Lu,Zihan Wei,Wendong Zhang,Koichi Suematsu,Jie Hu
DOI: https://doi.org/10.1016/j.snb.2024.136666
2025-01-01
Abstract:The construction of a novel Au nanoparticles loaded In2S3/In2O3 hybrid microflowers composite was conducted through a well-designed hydrothermal and partial oxidation method and used for NO2 sensing at room-temperature (RT). The characterization data confirmed the hybrid structures and demonstrated that the ratio of adsorbed oxygen species on the surface increased after partial oxidation. The sensing performance of flexible gas sensors based on In2S3/In2O3, In2O3, AuxIn2S3/In2O3 (x = 0.5, 1 and 2wt%) were tested and compared at RT. Heterostructure construction and Au NPs loading significantly improved the sensing properties at RT. Peculiarly, the response value of 1wt% Au NPs loaded In2S3/In2O3 (Au1In2S3/In2O3) sensor for 100 ppm NO2 at RT was 20.7, which was 9.2 times higher than that of In2O3 sensor. Meanwhile, it also possessed excellent selectivity, fast response/recovery time (12/27s), good repeatability, long-term and mechanical stability. The outstanding sensing performance for NO2 at RT mainly associated to the heterojunction between In2S3 and In2O3 and the catalytic effect of Au NPs. Finally, density functional theory (DFT) was used to calculate and analyze the gas adsorption and charger transfer, which related to the enhanced sensing performance.
What problem does this paper attempt to address?