Abstract:There is a significant need to elucidate the underlying mechanisms of cyclic plastic damage mechanism for additively manufactured materials and develop effective surface modification techniques to improve their fatigue life. This study investigates the efficacy of ultrasonic surface rolling process (USRP) technology in the creation of a ∼300 μm gradient nanotwinned structure on the surface of additively manufactured CoCrNi medium-entropy alloy (AM-MEA), which results in a beneficial result that yield strength and 10 7 -cycle fatigue endurance limit are significantly improved, achieving the increment of 192.1 MPa and ∼130 MPa, respectively. The superior fatigue property is attributed to multiple factors that suppress crack initiation from sample surfaces jointly, including the presence of a gradient nanotwinned layer and the reduction in irregular defects located both on and beneath the surface. The cyclic plastic deformation behavior of AM-MEA samples with and without USRP under both high and low stress levels was studied in-depth through multiscale characterization techniques. When exposed to cyclic loading at a low stress level of 480 MPa, the fatigue damages of both samples were dominated by accumulation of statistical stored dislocations (SSDs) and persistent Lüders bands. There is no significant difference in the increase in dislocation density between both samples. However, under cyclic loading at a high stress level (660 MPa), the fatigue damage of the AM-MEA sample primarily originated from the accumulation of deformation nanotwins, stacking faults, geometrically necessary dislocations and SSDs. Conversely, the fatigue damage observed in the AM-MEA sample with USRP at the same stress level was dominant by an increase in stacking faults and SSDs. Notably, this increase in total dislocation density was visibly lower than that observed in the AM-MEA sample, which is ascribe to the stable gradient layer providing enhanced hetero-deformation induced stress for the core region in the AM-MEA sample with USRP at high stress level.

Exploring the Strengthening Mechanisms of Additive Manufactured Metals Treated by Ultrasonic Nanocrystal Surface Modification

Achieving High Strength and High Ductility in Nanostructured Metals: Experiment and Modelling

Strain-induced Refinement and Thermal Stability of a Nanocrystalline Steel Produced by Surface Mechanical Attritiontreatment

Experimental Characterization and Strengthening Mechanism of Process-Structure-property of Selective Laser Melted 316 L

Enhancement of the Microstructure and Fatigue Crack Growth Performance of Additive Manufactured Titanium Alloy Parts by Laser-Assisted Ultrasonic Vibration Processing

Surface Nanocrystallization Mechanism of Additive Manufactured 316L Stainless Steel Via High-Energy Shot Peening

In-situ Study of Microstructure and Mechanical Properties of GH3536 Alloy Manufactured by Selective Laser Melting at 750 °C

Mechanical property enhancement in gradient structured aluminum alloy by ultrasonic nanocrystalline surface modification

Surface mechanical attrition treatment of additively manufactured 316L stainless steel yields gradient nanostructure with superior strength and ductility

Enhancement of fatigue resistance of additively manufactured 304L SS by unique heterogeneous microstructure

Deformation Mechanisms of Selective Laser Melted 316l Austenitic Stainless Steel in High Temperature Low Cycle Fatigue

Effects of ultrasonic nanocrystal surface modification on the surface integrity, microstructure, and wear resistance of 300M martensitic ultra-high strength steel

Effect of electropulsing-assisted ultrasonic nanocrystal surface modification on microstructures and hardness of additive manufactured Inconel 718

Magnetic-assisted Ultrasonic Nanocrystal Surface Modification Induced Microstructures of Titanium Alloy

Effects of ultrasonic shot peening process on the microstructure and mechanical properties of nickel-based superalloys formed by selective laser melting

Enhanced fatigue resistance and fatigue-induced substructures in an additively manufactured CoCrNi medium-entropy alloy treated by ultrasonic surface rolling process

The Effects of Laser‐Assisted Ultrasonic Nanocrystal Surface Modification on the Microstructure and Mechanical Properties of 300M Steel

Effects of Ultrasonic Nanocrystal Surface Modification on Surface Hardening Mechanism and Wear Behavior of Additively Manufactured High-Manganese Steel

A Novel Two-Stage Heat Treatment with Medium-Temperature Aging Influence on Microstructure, Al3(Sc, Zr) Nanoprecipitation, and Application Properties, Enhancing Selective Laser Melting of Al–Mg–Sc–Zr Alloy

Fatigue Performance Improvement of 7075-T651 Aluminum Alloy by Ultrasonic Nanocrystal Surface Modification

Enhanced strength–ductility synergy and transformation-induced plasticity of the selective laser melting fabricated 304L stainless steel