Abstract:Environmental barrier coatings (EBCs) are increasingly being used in the high-temperature sections of gas turbines because of their protective effects on SiC fiber-reinforced SiC ceramic matrix composites (SiCf/SiC CMCs) when subjected to high-temperature water oxygen corrosion. The objective of this study was to investigate the failure behavior of EBCs prepared on SiCf/SiC CMC matrix materials under coupled high-temperature and load conditions. A plasma spray-physical vapor deposition (PS-PVD) method was used to prepare Si/3Al2O3·2SiO2/Yb2SiO5 EBC composite coatings on the surface of SiCf/SiC ceramic matrix composites. In situ scanning electron microscopy was used to study the evolutionary behavior of the coating surface cracks at different temperatures and the failure and fracture mechanism of the coating/substrate when held at 766 °C and subjected to different loading conditions. The results show that no significant crack extension occurred on the coating surface as the temperature of the coated specimen increased from room temperature to 766 °C in the absence of an applied tensile load, indicating that the effect of a single temperature factor on the failure of the specimen was negligible. However, under coupled high-temperature and load conditions, the specimens fractured at a load of 340 N when subjected to 766 °C, indicating that the coated sample is more likely to fail when subjected to high-temperature and tensile loading. The step-like fracture exhibits features consistent with the coating fracture and spalling caused by surface cracks extending from the coating surface to the interior. The spalling, large crack formation and step-like shape of the fracture in the coating and the substrate indicate that cracks were generated between the coating and the substrate under the coupled high-temperature and load conditions. The generation and extension of cracks in both parts eventually led to full specimen rupture.

High-temperature Oxidation Behavior and Mechanical Properties of PS-PVD Sprayed Yb2Si2O7 Environmental Barrier Coatings

Characterization of Yb2SiO5-based environmental barrier coating prepared by plasma spray–physical vapor deposition

Corrosion behavior of PS-PVD spray Yb2Si2O7 environmental barrier coatings during continuous water vapor exposure

Oxidation behavior and interface evolution of tri-layer Si/Yb2SiO5/LaMgAl11O19 thermal and environmental barrier coatings under isothermal heat treatment at 1300 °C

Oxidation behaviors and mechanisms of Yb2O3-doped silicon coatings fabricated by vacuum plasma spray

Thermal cycle and water oxygen performance of multi-layered Y3Al5O12/Yb2SiO5/Yb2Si2O7 thermal/environmental barrier coatings

Water Vapor Corrosion Behavior of Yb2SiO5 Environmental Barrier Coatings Prepared by Plasma Spray-Physical Vapor Deposition

Oxidation resistance and thermal shock behavior of tri-layer Si/Si–Yb2SiO5/Yb2SiO5–SiC environmental barrier coatings at 1300 °C

Thermochemical Stability of Yb 2 Si 2 O 7 Environmental Barrier Coatings During Thermal Cycling and Water Vapor Corrosion at 1350 °C

In Situ High-Temperature Tensile Fracture Mechanism of PS-PVD EBCs

Rear Earth Oxide Multilayer Deposited by Plasma Spray-Physical Vapor Deposition for Envisaged Application as Thermal/Environmental Barrier Coating

Corrosion behavior and mechanism of ytterbium silicates environmental barrier coatings to thermal cycling in water vapor

Mechanism of vertical crack formation in Yb2SiO5 coatings deposited via plasma spray-physical vapor deposition

Microstructure and Thermal Property Evolution of Plasma-Sprayed Lu2SiO5 EBCs Under High Temperature Environments

Failure behaviour of EB-PVD YSZ thermal barrier coatings under simulated aero-engine operating conditions

Cyclic oxidation and water vapor corrosion behaviors of multi-layer environmental barrier coatings with HfO2-Si bond coat for SiCf/SiC

Yb2SiO5-Yb2Si2O7 Gradient Environment Barrier Coating ： Rational Design and Corrosion Behavior in Water Vapor Environment at 1300 ℃

Thermal cycling and steam corrosion behavior of Yb3Al5O12‐based multilayered environmental barrier coatings for SiCf/SiC

Effect of Sc2O3 Doping on YSZ TBCs: Morphologies, Phase Composition, Mechanical Properties, and High-Temperature Oxidation Resistance

Realizing the Excellent Oxidation Resistance of an Environmental Barrier Coating Through Aluminum Surface Modification

High-temperature performance of thermal environmental barrier coatings in 90%H2O-10%O2 conditions at 1475 °C